General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.25 g/cm³ Show Material materials with Densidad of 1.25 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.48 [-] Show Material materials with Coeficiente de Poisson of 0.48 [-] | |
Dureza Shore D | 23.0 °C | 61 [-] Show Material materials with Dureza Shore D of 61 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 290 % Show Material materials with Elongación of 290 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 0.17 GPa Show Material materials with Módulo de flexión of 0.17 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.19 GPa Show Material materials with Módulo elástico of 0.19 GPa | ISO 527-1/-2 |
Resistencia a desgarros | 23.0 °C | 170 kN/m Show Material materials with Resistencia a desgarros of 170 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 175 kN/m Show Material materials with Resistencia a desgarros transversal of 175 kN/m | ISO 34-1 |
Resistencia a la tracción | 23.0 °C | 32 MPa Show Material materials with Resistencia a la tracción of 32 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 3.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 3.5 kJ/m² | ISO 179/1eA |
-6.0 °C | 4.5 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 4.5 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 4 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 4 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Brittleness temperature | -65 °C Show Material materials with Brittleness temperature of -65 °C | ISO 974 | |
Heat deflection temperature, 0.45 MPa | 47 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 47 °C | ISO 75-1/-2 | |
Temperatura de fusión | 165 °C Show Material materials with Temperatura de fusión of 165 °C | ISO 11357-1/-3 | 18°F/min | |
Temperatura de reblandecimiento Vicat | 130 °C Show Material materials with Temperatura de reblandecimiento Vicat of 130 °C | ISO 306 | 90°F, 2 lbf | |
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min | ||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.3 % Show Material materials with Contracción of 0.3 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 0.7 % Show Material materials with Contracción transversal of 0.7 % | ISO 294-4, 2577 |
Velocidad de flujo del volumen derretido | 5.2 cm³/10min Show Material materials with Velocidad de flujo del volumen derretido of 5.2 cm³/10min | ISO 1133 |
Technological properties
| Property | ||
|---|---|---|
| Processing methods | Drying Recommended: yes, Drying Temperature: 90°C, Drying Time, Dehumidified Dryer: 2-3h, Processing Moisture Content: ≤0.08%, Melt Temperature Optimum: 200°C, Min. melt temperature: 185°C, Max. melt temperature: 215°C, Mold Temperature Optimum: 45°C, Min. mold temperature: 40°C, Max. mold temperature: 55°C | |