General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.16 g/cm³ Show Material materials with Densidad of 1.16 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.48 [-] Show Material materials with Coeficiente de Poisson of 0.48 [-] | |
Dureza Shore D | 23.0 °C | 60 [-] Show Material materials with Dureza Shore D of 60 [-] | max., ISO 7619-1 |
Elongación | 23.0 °C | 300 % Show Material materials with Elongación of 300 % | ISO 527-1/-2 |
Módulo de flexión | 23.0 °C | 0.27 GPa Show Material materials with Módulo de flexión of 0.27 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 0.27 GPa Show Material materials with Módulo elástico of 0.27 GPa | ISO 527-1/-2 |
Resistencia a desgarros | 23.0 °C | 140 kN/m Show Material materials with Resistencia a desgarros of 140 kN/m | ISO 34-1 |
Resistencia a desgarros transversal | 23.0 °C | 130 kN/m Show Material materials with Resistencia a desgarros transversal of 130 kN/m | ISO 34-1 |
Resistencia a la tracción | 23.0 °C | 33 MPa Show Material materials with Resistencia a la tracción of 33 MPa | ISO 527-1/-2 |
Resistencia al choque, ensayo Charpy entallado | -40.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA |
-6.0 °C | 12 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | |
23.0 °C | 102 kJ/m² Show Material materials with Resistencia al choque, ensayo Charpy entallado of 102 kJ/m² | ISO 179/1eA | |
Resistencia al choque, ensayo Izod no entallado | -40.0 °C | 7 kJ/m² Show Material materials with Resistencia al choque, ensayo Izod no entallado of 7 kJ/m² | ISO 180/1A |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Brittleness temperature | -65 °C Show Material materials with Brittleness temperature of -65 °C | ISO 974 | |||
Coeficiente de dilatación térmica | 23.0 °C | 2E-4 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.8E-4 1/K Show Material materials with Coeficiente de dilatación térmica transversal of 1.8E-4 1/K | ISO 11359-1/-2 | -40 - 23°C | ||
Heat deflection temperature, 0.45 MPa | 65 °C Show Material materials with Heat deflection temperature, 0.45 MPa of 65 °C | ISO 75-1/-2 | |||
Heat deflection temperature, 1.80 MPa | 45 °C Show Material materials with Heat deflection temperature, 1.80 MPa of 45 °C | ISO 75-1/-2 | |||
Temperatura de fusión | 215 °C Show Material materials with Temperatura de fusión of 215 °C | ISO 11357-1/-3 | 18°F/min | |||
Temperatura de reblandecimiento Vicat | 195 °C Show Material materials with Temperatura de reblandecimiento Vicat of 195 °C | ISO 306 | 90°F, 2 lbf | |||
Temperatura de transición del vidrio | 15 °C Show Material materials with Temperatura de transición del vidrio of 15 °C | ISO 11357-1/-2 | 18°F/min | |||
Inflamabilidad | FMVSS Class: B -, Burning rate, Thickness 1 mm: <80 mm/min |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 2.4 % Show Material materials with Contracción of 2.4 % | ISO 294-4, 2577 |
Contracción transversal | 23.0 °C | 2.2 % Show Material materials with Contracción transversal of 2.2 % | ISO 294-4, 2577 |
Velocidad de flujo de la masa derretida | 4 g/10min Show Material materials with Velocidad de flujo de la masa derretida of 4 g/10min | ISO 1133 | 240°C/10kg |
Technological properties
Property |
---|