General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 10.28 g/cm³ Show Material materials with Densidad of 10.28 g/cm³ |
Medidas
Property | Value |
---|---|
Espesor | 4.8 - 25.4 mm Show Material materials with Espesor of 4.8 - 25.4 mm |
Dimensions | Available thicknesses: 4.8mm, 6.4mm, 7.9mm, 9.5mm, 12.7mm, 15.9mm, 19.1mm, 25.4mm |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Vickers | 23.0 °C | 220 [-] Show Material materials with Dureza Vickers of 220 [-] | |
Elongación | 23.0 °C | 12 % Show Material materials with Elongación of 12 % | in 1 in. |
Módulo elástico | 23.0 °C | 320 GPa Show Material materials with Módulo elástico of 320 GPa | |
Resistencia a la tracción | 20.0 °C | 1035 MPa Show Material materials with Resistencia a la tracción of 1035 MPa | |
500.0 °C | 515 MPa Show Material materials with Resistencia a la tracción of 515 MPa | ||
1000.0 °C | 175 MPa Show Material materials with Resistencia a la tracción of 175 MPa | ||
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 259 J/(kg·K) Show Material materials with Calor específico of 259 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 4.8E-6 1/K Show Material materials with Coeficiente de dilatación térmica of 4.8E-6 1/K |
Conductividad térmica | 23.0 °C | 142 W/(m·K) Show Material materials with Conductividad térmica of 142 W/(m·K) |
Temperatura de cristalización | 1100 °C Show Material materials with Temperatura de cristalización of 1100 °C | |
Temperatura de fusión | 2623 °C Show Material materials with Temperatura de fusión of 2623 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 200.0 °C | 5.34E-8 Ω·m Show Material materials with Resistividad eléctrica of 5.34E-8 Ω·m |
Chemical properties
Property | Value | Comment |
---|---|---|
Molibdeno | 99.97 % Show Material materials with Molibdeno of 99.97 % | min |
Technological properties
Property | ||
---|---|---|
Application areas | In the missile industry Molybdenum is used for nose cones, high temperature structural parts, nozzles, leading edges of control surfaces, support vanes, re-entry cones, and heat radiation shields. In electronics Molybdenum is used for cathodes, magnetron end hats, x-ray tube components, filaments, and glass-to-metal seals. In high-temperature applications Molybdenum is used for: furnace windings, structural furnace members, and containers for components exposed to high temperatures. |