General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 1.6 % Show Material materials with Absorción de agua of 1.6 % | for 54h to boiling water |
Densidad | 23.0 °C | 1.17 g/cm³ Show Material materials with Densidad of 1.17 g/cm³ | ASTM D792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 4 - 7.2 % Show Material materials with Elongación of 4 - 7.2 % | |||
Módulo elástico | 23.0 °C | 3.1 GPa Show Material materials with Módulo elástico of 3.1 GPa | ASTM D638 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 0.62 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 0.62 MPa·√m | ASTM D5045 | ||
Resistencia a la flexión | 23.0 °C | 152 MPa Show Material materials with Resistencia a la flexión of 152 MPa | ASTM D790 | ||
Resistencia a la tracción | 23.0 °C | 95 MPa Show Material materials with Resistencia a la tracción of 95 MPa | ASTM D638 | ||
Liberación de energía de deformación | ASTM D5045 | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.2E-5 1/K | ASTM E831 | ||
Temperatura de transición del vidrio | 202 °C Show Material materials with Temperatura de transición del vidrio of 202 °C | ASTM E1640 | |||
Temperatura máx. de funcionamiento | 150 | ||||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Drones;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel | |
| Processing history | Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool. | |
| Processing methods | Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool. | |