Structural Epoxy Resin T26 (EP-CF)

Want to keep this datasheet? Save it now in your required format

Description

Т26 is a single part low viscosity epoxy infusion carbon fiber reinforced resin developed for high-loaded structures. T26 offers simple and flexible processing due to low viscosity at relatively low impregnation temperatures (110°С). T26 was developed specially for RTM and vacuum infusion molding, to produce laminates with low porosity and extremely high mechanical performance, especially in crack resistance. It shows the following features and properties:

One-part resin designed specifically for high-temperature infusion or RTM

Wide processing window > 7 hours at 110°C

Curing at 180°C provides glass transition temperature of 205°C

High wet glass transition temperature —172°C

Very high resistance to impact

Operating temperatures from –60°C to 150°C

Los datos sobre este material han sido proporcionados por Matmatch.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Propiedades

Mecánica

Property	Temperature	Value	Comment
Módulo elástico	23.0 °C	65 GPa Show Material materials with Módulo elástico of 65 GPa	ASTM D3039
Módulo elástico transversal	23.0 °C	66 GPa Show Material materials with Módulo elástico transversal of 66 GPa	ASTM D3039
Resistencia a la compresión	23.0 °C	643 MPa Show Material materials with Resistencia a la compresión of 643 MPa	ASTM D6641
Resistencia a la compresión transversal	23.0 °C	679 MPa Show Material materials with Resistencia a la compresión transversal of 679 MPa	ASTM D6641
Resistencia a la tracción	23.0 °C	910 MPa Show Material materials with Resistencia a la tracción of 910 MPa	ASTM D3039
Resistencia a la tracción transversal	23.0 °C	881 MPa Show Material materials with Resistencia a la tracción transversal of 881 MPa	ASTM D3039
Shear modulus, G₁₂	23.0 °C	4.5 GPa Show Material materials with Shear modulus, G₁₂ of 4.5 GPa	ASTM D5379
Shear strength, τ₁₂	23.0 °C	84 MPa Show Material materials with Shear strength, τ₁₂ of 84 MPa
Shear strength, τ₁₃	25.0 °C	74 MPa Show Material materials with Shear strength, τ₁₃ of 74 MPa	ASTM D2344
	120.0 °C	51 MPa Show Material materials with Shear strength, τ₁₃ of 51 MPa	ASTM D2344
	150.0 °C	45 MPa Show Material materials with Shear strength, τ₁₃ of 45 MPa	ASTM D2344

Liberación de energía de deformación	ASTM D5528

Technological properties

Property
Application areas	Drones;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite;Geometry strengthen elements: Experimental stringer panel
Processing history	Samples for testing were obtained by vacuum infusion based on T26 resin and carbon fabric (CF) 22508 (sateen 8H, 200 g/m2, 3K, 3.95 GPa).
Processing methods	Preheat the resin to 60-90°С in its container for transfer to the resin pot. Degas the resin for 30-40 minutes while heating to 90°С. Preheat the tool to 100-110°С (or to 115-120°С for parts having complex shape or for UD parts). Maintaining resin pot temperature of 95 °С and tool temperature of 100-115 °С, begin resin infusion. After complete impregnation increase tool temperature at 2°С/min to 180°С. Dwell at 180°С for 3 h. Cool the tool to 90°С at <5°С/min before releasing part from tool.

Structural Epoxy Resin T26 (EP-CF)