General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.34 g/cm³ Show Material materials with Densidad of 1.34 g/cm³ | ASTM D792 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Módulo de flexión | 23.0 °C | 4.6 GPa Show Material materials with Módulo de flexión of 4.6 GPa | ASTM D790 | ||
Módulo elástico | 23.0 °C | 4.8 GPa Show Material materials with Módulo elástico of 4.8 GPa | ASTM D638 | ||
Plane-Strain Fracture Toughnes | 23.0 °C | 0.76 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 0.76 MPa·√m | ASTM D5045 | ||
Resistencia a la flexión | 23.0 °C | 4.6 MPa Show Material materials with Resistencia a la flexión of 4.6 MPa | ASTM D790 | ||
Resistencia a la tracción | 23.0 °C | 60 MPa Show Material materials with Resistencia a la tracción of 60 MPa | ASTM D638 | ||
Liberación de energía de deformación | ASTM D5045 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ASTM E831 |
Temperatura de flexión bajo carga | 200 °C Show Material materials with Temperatura de flexión bajo carga of 200 °C | ASTM E2092 | |
Temperatura de reblandecimiento Vicat | 80 °C Show Material materials with Temperatura de reblandecimiento Vicat of 80 °C |
Magnético
Property | Value |
---|---|
Temperatura de Curie | 180 °C Show Material materials with Temperatura de Curie of 180 °C |
Technological properties
Property | ||
---|---|---|
Application areas | Structures requiring high heat resistance;Parts requiring non-combustibility;Parts of engines and other special applications;High temperature tooling for thermoplastics | |
Processing methods | Assemble the vacuum bag. Perform a leak test, the rate of the vacuum drop should not be more than 1 mbar per minute. The residual pressure in the bag must not be more than 10 mbar. Assemble the second vacuum bag, put airweave material between the layers of the vacuum film. Perform a leak test for the second vacuum bag. The residual pressure in the bag must not be more than 10 mbar. Degas for 30-40 minutes, at 150-160°C, at a pressure of no more than 10 mbar. During the degassing, the resin should be stirred intensively. Heat the tool up to 150-170°C. Maintaining the temperature of resin dispenser at 160°C, start the infusion process. After complete impregnation of the bag, close the resin inputs, but continue evacuation from the inner bag for at least 30 minutes. Then close the outputs from the inner bag. Maintain the outer vacuum bag until the end of curing process. Increase the temperature at a rate of 2°C/min to 180°C. Dwell at 180°C for 6 hours. Before removing the part, cool the mold to at least 60°C at a speed of no more than 5°C/min. Post-cure can be performed without tooling. Heat to 180°C at a rate of 2°C/min, then heat to 375°C at a rate of 5-10°C/min. Dwell at 375°C for 8 hours. Cool down the part to 60°C at rate <5°C/min. For the measurement of vacuum, the use of absolute pressure sensors is recommended. |