ОоА prepreg B180 CF08 [0,+45]nS

Want to keep this datasheet? Save it now in your required format

Description

В180 is a prepreg based on epoxy carbon fiber reinforced resin for producing details with operating temperatures up to 150°C. Out-of-autoclave prepreg technology has the most advantages of autoclave. The autoclave is not required for processing the prepreg B180. Curing takes place in a vacuum bag, with the technology of the package laminating slightly different from the vacuum infusion. It shows the following features and properties:

High mechanical performance

Possibility of application in loaded parts at service temperatures up to 120°C

Less stringent requirements for working staff

Glass transition temperature 154°C

Out of autoclave processing

Los datos sobre este material han sido proporcionados por Matmatch.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Propiedades

Mecánica

Property	Temperature	Value	Comment
Módulo de compresión	23.0 °C	71 MPa Show Material materials with Módulo de compresión of 71 MPa	ASTM D695, Lamina
Módulo elástico	23.0 °C	60 GPa Show Material materials with Módulo elástico of 60 GPa	ASTM D3039, Lamina
Resistencia a la compresión	23.0 °C	802 MPa Show Material materials with Resistencia a la compresión of 802 MPa	ASTM D6641, Lamina
Resistencia a la tracción	23.0 °C	871 MPa Show Material materials with Resistencia a la tracción of 871 MPa	ASTM D3039, Lamina
Shear modulus, G₁₂	23.0 °C	5.7 GPa Show Material materials with Shear modulus, G₁₂ of 5.7 GPa	ASTM D5379, Lamina
Shear strength, τ₁₂	23.0 °C	126 MPa Show Material materials with Shear strength, τ₁₂ of 126 MPa
Shear strength, τ₁₃	23.0 °C	79 MPa Show Material materials with Shear strength, τ₁₃ of 79 MPa	ASTM D2344, Lamina
Shear strength, τ₁₃ laminate	25.0 °C	66 MPa Show Material materials with Shear strength, τ₁₃ laminate of 66 MPa
	85.0 °C	59 MPa Show Material materials with Shear strength, τ₁₃ laminate of 59 MPa

Tensile strength laminate	25.0 °C	668 MPa Show Material materials with Tensile strength laminate of 668 MPa
	85.0 °C	670 MPa Show Material materials with Tensile strength laminate of 670 MPa
	Unlock all property charts

Technological properties

Property
Application areas	Marine: The shells of boats and sport catamarans can be made of composites;Car tuning: The composite material provides solutions for automotive parts to be light-weighted, stylish and aesthetic;Sports equipment: Frame, wheels, seat, seat post, handlebar, head stem and crank arm of a sports bicycle are made of carbon composite
Processing history	Reinforcing filler: carbon fabric 22508 (twill 2x2, 200 g/m2, HTA40). Carbon plastic is produced by vacuum molding.
Processing methods	Holding at a temperature of 25-30°C, for 12 hours, a vacuum of -1 bar. Heating 2°C/min. up to 120°C, holding at 120°C for 180 minutes. Heating 2°C/min. up to 180°C, holding at 180°C for 180 minutes, cooling no faster than 5°C/min. up to 50°С.