General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.18 g/cm³ Show Material materials with Densidad of 7.18 g/cm³ | Typical for Wrought Zinc Grade |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-] | Typical for Magnesium |
Elongación A50 | 23.0 °C | 4 - 7 % Show Material materials with Elongación A50 of 4 - 7 % | |
Límite elástico Rp 0,2 | 23.0 °C | 179 - 221 MPa Show Material materials with Límite elástico Rp 0,2 of 179 - 221 MPa | |
Módulo de cizallamiento | 23.0 °C | 45 GPa Show Material materials with Módulo de cizallamiento of 45 GPa | Typical for Magnesium |
Módulo elástico | 23.0 °C | 40 - 45 GPa Show Material materials with Módulo elástico of 40 - 45 GPa | Typical for Wrought Zinc Grade |
Resistencia a la tracción | 23.0 °C | 290 - 296 MPa Show Material materials with Resistencia a la tracción of 290 - 296 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 1050 J/(kg·K) Show Material materials with Calor específico of 1050 J/(kg·K) | Typical for Wrought Zinc Grade |
Coeficiente de dilatación térmica | 23.0 °C | 2.7E-5 - 2.72E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.7E-5 - 2.72E-5 1/K | Typical for Wrought Zinc Grade |
Conductividad térmica | 23.0 °C | 117 - 146 W/(m·K) Show Material materials with Conductividad térmica of 117 - 146 W/(m·K) | Typical for Wrought Zinc Grade |
Temperatura de fusión | 520 - 635 °C Show Material materials with Temperatura de fusión of 520 - 635 °C | Typical for Wrought Zinc Grade |
Chemical properties
Property | Value |
---|---|
Circonio | 0.45 % Show Material materials with Circonio of 0.45 % |
Zinc | 4.8 - 6.2 % Show Material materials with Zinc of 4.8 - 6.2 % |