General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.8 g/cm³ Show Material materials with Densidad of 7.8 g/cm³ | Typical for Duplex Stainless Steel |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.3 [-] Show Material materials with Coeficiente de Poisson of 0.3 [-] | Typical for Duplex Stainless Steel |
Elongación | 23.0 °C | 18 % Show Material materials with Elongación of 18 % | |
Límite elástico | 23.0 °C | 392 MPa Show Material materials with Límite elástico of 392 MPa | |
Módulo de cizallamiento | 23.0 °C | 77 GPa Show Material materials with Módulo de cizallamiento of 77 GPa | Typical for Duplex Stainless Steel |
Módulo elástico | 23.0 °C | 200 GPa Show Material materials with Módulo elástico of 200 GPa | Typical for Duplex Stainless Steel |
Resistencia a la tracción | 23.0 °C | 588 MPa Show Material materials with Resistencia a la tracción of 588 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 440 - 502 J/(kg·K) Show Material materials with Calor específico of 440 - 502 J/(kg·K) | Typical for Duplex Stainless Steel |
Coeficiente de dilatación térmica | 23.0 °C | 1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-5 1/K | Typical for Duplex Stainless Steel |
Conductividad térmica | 23.0 °C | 13 - 30 W/(m·K) Show Material materials with Conductividad térmica of 13 - 30 W/(m·K) | Typical for Duplex Stainless Steel |
Temperatura de fusión | 1375 - 1450 °C Show Material materials with Temperatura de fusión of 1375 - 1450 °C | Typical for Duplex Stainless Steel | |
Temperatura máx. de funcionamiento | 300 °C Show Material materials with Temperatura máx. de funcionamiento of 300 °C | Typical for Duplex Stainless Steel |
Technological properties
Property | ||
---|---|---|
Processing history | hot-rolled and solution annealed |