Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.8 - 7.9 g/cm³ Show Material materials with Densidad of 7.8 - 7.9 g/cm³ | Typical for Chromium Molybdenum Steel |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-] | Typical for Chromium Molybdenum Steel |
Elongación | 20.0 °C | 10 - 13 % Show Material materials with Elongación of 10 - 13 % | |
Elongación transversal | 20.0 °C | 8 - 11 % Show Material materials with Elongación transversal of 8 - 11 % | |
Estricción | 20.0 °C | 40 - 50 % Show Material materials with Estricción of 40 - 50 % | |
Límite elástico | 20.0 °C | 550 - 900 MPa Show Material materials with Límite elástico of 550 - 900 MPa | |
Límite elástico transversal | 20.0 °C | 550 - 900 MPa Show Material materials with Límite elástico transversal of 550 - 900 MPa | |
Módulo elástico | 23.0 °C | 200 - 215 GPa Show Material materials with Módulo elástico of 200 - 215 GPa | Typical for Chromium Molybdenum Steel |
Reducción de área, transversal | 20.0 °C | 40 - 50 % Show Material materials with Reducción de área, transversal of 40 - 50 % | |
Resistencia a la tracción | 20.0 °C | 800 - 1300 MPa Show Material materials with Resistencia a la tracción of 800 - 1300 MPa | |
Resistencia a la tracción transversal | 20.0 °C | 800 - 1300 MPa Show Material materials with Resistencia a la tracción transversal of 800 - 1300 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 448 - 502 J/(kg·K) Show Material materials with Calor específico of 448 - 502 J/(kg·K) | Typical for Chromium Molybdenum Steel |
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-5 - 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-5 - 1.4E-5 1/K | Typical for Chromium Molybdenum Steel |
Conductividad térmica | 23.0 °C | 36 - 43 W/(m·K) Show Material materials with Conductividad térmica of 36 - 43 W/(m·K) | Typical for Chromium Molybdenum Steel |
Temperatura de fusión | 1382 - 1529 °C Show Material materials with Temperatura de fusión of 1382 - 1529 °C | Typical for Chromium Molybdenum Steel |
Chemical properties
Property | Value |
---|---|
Azufre | 0.035 % Show Material materials with Azufre of 0.035 % |
Carbono | 0.38 - 0.45 % Show Material materials with Carbono of 0.38 - 0.45 % |
Cromo | 0.9 - 1.2 % Show Material materials with Cromo of 0.9 - 1.2 % |
Fósforo | 0.04 % Show Material materials with Fósforo of 0.04 % |
Manganeso | 0.6 - 0.9 % Show Material materials with Manganeso of 0.6 - 0.9 % |
Molibdeno | 0.15 - 0.3 % Show Material materials with Molibdeno of 0.15 - 0.3 % |
Silicona | 0.4 % Show Material materials with Silicona of 0.4 % |