DIN 1693-1 Grade GGG-40 cast condition

Want to keep this datasheet? Save it now in your required format

Description

GGG-40, a ferritic cast iron material with nodular cast iron for cast pieces for high performance with the mechanical treatment as well as for cast pieces with high strain at rupture and impact energy for static and dynamic loadings in the construction of vehicles, building of ships, in civil engineering, plastics processing, for pumps and compressors as well as for armatures, in the machine tool manufacture, mechanical engineering, energy mechanical engineering, in the casting industry. For engine bearings, articulated bearing, disk wheels, axles, transmission case, engine racks, front plates, lockcylinder, framework, pump housing, cylinder, impellers, chuck, stand for machine tools, transport and storage vessel, molding boxes, molds, rims, hydraulic housing etc.. The material is comparable to UNS F 32800 of the USA.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Comment
Densidad	23.0 °C	7.15 g/cm³ Show Material materials with Densidad of 7.15 g/cm³	Typical for Ductile (Nodular) Cast Iron

Mecánica

Property	Temperature	Value	Comment
Coeficiente de Poisson	20.0 °C	0.27 - 0.29 [-] Show Material materials with Coeficiente de Poisson of 0.27 - 0.29 [-]
Compressive yield strength	20.0 °C	700 MPa Show Material materials with Compressive yield strength of 700 MPa
Dureza Brinell	20.0 °C	135 - 185 [-] Show Material materials with Dureza Brinell of 135 - 185 [-]
Elongación	20.0 °C	15 % Show Material materials with Elongación of 15 %
Límite elástico	20.0 °C	250 MPa Show Material materials with Límite elástico of 250 MPa
Módulo de cizallamiento	23.0 °C	63 - 66 GPa Show Material materials with Módulo de cizallamiento of 63 - 66 GPa	Typical for Ductile (Nodular) Cast Iron
Módulo elástico	23.0 °C	165 - 180 GPa Show Material materials with Módulo elástico of 165 - 180 GPa	Typical for Ductile (Nodular) Cast Iron
Resistencia a la tracción	20.0 °C	400 MPa Show Material materials with Resistencia a la tracción of 400 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	460 - 502 J/(kg·K) Show Material materials with Calor específico of 460 - 502 J/(kg·K)	Typical for Ductile (Nodular) Cast Iron
Coeficiente de dilatación térmica	100.0 °C	1.28E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.28E-5 1/K
	200.0 °C	1.33E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.33E-5 1/K
	300.0 °C	1.38E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.38E-5 1/K
	400.0 °C	1.43E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.43E-5 1/K
	500.0 °C	1.48E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.48E-5 1/K

Conductividad térmica	100.0 °C	38 W/(m·K) Show Material materials with Conductividad térmica of 38 W/(m·K)
	200.0 °C	39 W/(m·K) Show Material materials with Conductividad térmica of 39 W/(m·K)
	300.0 °C	37 W/(m·K) Show Material materials with Conductividad térmica of 37 W/(m·K)
	400.0 °C	36 W/(m·K) Show Material materials with Conductividad térmica of 36 W/(m·K)
	500.0 °C	34 W/(m·K) Show Material materials with Conductividad térmica of 34 W/(m·K)
	Unlock all property charts
Temperatura de fusión		1150 - 1200 °C Show Material materials with Temperatura de fusión of 1150 - 1200 °C	Typical for Ductile (Nodular) Cast Iron

Chemical properties

Property	Value
Azufre	0.01 % Show Material materials with Azufre of 0.01 %
Carbono	3.5 - 3.8 % Show Material materials with Carbono of 3.5 - 3.8 %
Fósforo	0.1 % Show Material materials with Fósforo of 0.1 %
Magnesio	0.06 - 0.12 % Show Material materials with Magnesio of 0.06 - 0.12 %
Manganeso	0.4 % Show Material materials with Manganeso of 0.4 %
Silicona	2 - 3 % Show Material materials with Silicona of 2 - 3 %