SEW 395 Grade G-X120Mn13 solution heat-treated and quenched

Want to keep this datasheet? Save it now in your required format

Description

The fully austenitic material G-X 120 Mn 13 possesses a defined low value of the relative magnetic permeability of 1.01 maximum (for castings with a wall thickness of up to 50 mm). It is applied for construction components which an interference or shielding of a magnetic field must not occur at. To a large extent, the austenitic manganese cast steel is applied as a wear-resistant material. Its toughness is quite good, its resistance to corrosion in water is bad, welding is possible. Because of the strong strain hardening, the metal-removing machinability poses difficulties.

Related Standards

SEW 395

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value
Densidad	20.0 °C	7.9 g/cm³ Show Material materials with Densidad of 7.9 g/cm³

Mecánica

Property	Temperature	Value	Comment
Coeficiente de Poisson	23.0 °C	0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-]	Typical for Manganese Steel
Elongación	20.0 °C	25 % Show Material materials with Elongación of 25 %
Límite elástico Rp 0,2	20.0 °C	295 MPa Show Material materials with Límite elástico Rp 0,2 of 295 MPa
Módulo elástico	23.0 °C	200 - 215 GPa Show Material materials with Módulo elástico of 200 - 215 GPa	Typical for Manganese Steel
Resistencia a la tracción	20.0 °C	590 MPa Show Material materials with Resistencia a la tracción of 590 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	510 - 553 J/(kg·K) Show Material materials with Calor específico of 510 - 553 J/(kg·K)	Typical for Manganese Steel
Coeficiente de dilatación térmica	100.0 °C	1.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.8E-5 1/K
	200.0 °C	1.9E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.9E-5 1/K
	300.0 °C	2E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2E-5 1/K

Conductividad térmica	20.0 °C	15 W/(m·K) Show Material materials with Conductividad térmica of 15 W/(m·K)
Temperatura de fusión		1382 - 1529 °C Show Material materials with Temperatura de fusión of 1382 - 1529 °C	Typical for Manganese Steel
Temperatura máx. de funcionamiento, largo		0 - 300 °C Show Material materials with Temperatura máx. de funcionamiento, largo of 0 - 300 °C

Eléctrico

Property	Temperature	Value
Resistividad eléctrica	20.0 °C	8E-7 Ω·m Show Material materials with Resistividad eléctrica of 8E-7 Ω·m

Chemical properties

Property	Value
Azufre	0.03 % Show Material materials with Azufre of 0.03 %
Carbono	1.1 - 1.3 % Show Material materials with Carbono of 1.1 - 1.3 %
Cromo	0.5 % Show Material materials with Cromo of 0.5 %
Fósforo	0.06 % Show Material materials with Fósforo of 0.06 %
Manganeso	11.5 - 13.5 % Show Material materials with Manganeso of 11.5 - 13.5 %
Silicona	0.5 % Show Material materials with Silicona of 0.5 %