General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.15 g/cm³ Show Material materials with Densidad of 7.15 g/cm³ | Typical for Ductile (Nodular) Cast Iron |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.26 - 0.31 [-] Show Material materials with Coeficiente de Poisson of 0.26 - 0.31 [-] | Typical for Ductile (Nodular) Cast Iron |
Dureza Brinell | 23.0 °C | 401 [-] Show Material materials with Dureza Brinell of 401 [-] | |
Elongación A5 | 23.0 °C | 1 % Show Material materials with Elongación A5 of 1 % | |
Límite elástico | 23.0 °C | 1100 MPa Show Material materials with Límite elástico of 1100 MPa | |
Módulo de cizallamiento | 23.0 °C | 63 - 66 GPa Show Material materials with Módulo de cizallamiento of 63 - 66 GPa | Typical for Ductile (Nodular) Cast Iron |
Módulo elástico | 23.0 °C | 165 - 180 GPa Show Material materials with Módulo elástico of 165 - 180 GPa | Typical for Ductile (Nodular) Cast Iron |
Resistencia a la tracción | 23.0 °C | 1400 MPa Show Material materials with Resistencia a la tracción of 1400 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 460 - 502 J/(kg·K) Show Material materials with Calor específico of 460 - 502 J/(kg·K) | Typical for Ductile (Nodular) Cast Iron |
Coeficiente de dilatación térmica | 23.0 °C | 1E-5 - 1.6E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-5 - 1.6E-5 1/K | Typical for Ductile (Nodular) Cast Iron |
Conductividad térmica | 23.0 °C | 13 - 42 W/(m·K) Show Material materials with Conductividad térmica of 13 - 42 W/(m·K) | Typical for Ductile (Nodular) Cast Iron |
Temperatura de fusión | 1150 - 1200 °C Show Material materials with Temperatura de fusión of 1150 - 1200 °C | Typical for Ductile (Nodular) Cast Iron |