General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.2 - 7.34 g/cm³ Show Material materials with Densidad of 7.2 - 7.34 g/cm³ | Typical for Malleable Cast Iron |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.27 [-] Show Material materials with Coeficiente de Poisson of 0.27 [-] | Typical for Malleable Cast Iron |
Dureza Brinell | 23.0 °C | 207 - 269 [-] Show Material materials with Dureza Brinell of 207 - 269 [-] | |
Elongación A5 | 23.0 °C | 3 % Show Material materials with Elongación A5 of 3 % | |
Límite elástico Rp 0,2 | 23.0 °C | 390 MPa Show Material materials with Límite elástico Rp 0,2 of 390 MPa | |
Módulo de cizallamiento | 23.0 °C | 64 GPa Show Material materials with Módulo de cizallamiento of 64 GPa | Typical for Malleable Cast Iron |
Módulo elástico | 23.0 °C | 165 - 180 GPa Show Material materials with Módulo elástico of 165 - 180 GPa | Typical for Malleable Cast Iron |
Resistencia a la tracción | 23.0 °C | 590 MPa Show Material materials with Resistencia a la tracción of 590 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 460 - 527 J/(kg·K) Show Material materials with Calor específico of 460 - 527 J/(kg·K) | Typical for Malleable Cast Iron |
Coeficiente de dilatación térmica | 23.0 °C | 1E-5 - 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1E-5 - 1.4E-5 1/K | Typical for Malleable Cast Iron |
Conductividad térmica | 23.0 °C | 51 W/(m·K) Show Material materials with Conductividad térmica of 51 W/(m·K) | Typical for Malleable Cast Iron |
Temperatura de fusión | 1120 °C Show Material materials with Temperatura de fusión of 1120 °C | Typical for Cast Iron |