General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 7.75 - 8.4 g/cm³ Show Material materials with Densidad of 7.75 - 8.4 g/cm³ | Typical for Nickel Chromium Iron Alloy |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación A50 | 23.0 °C | 4.5 % Show Material materials with Elongación A50 of 4.5 % | |
Límite elástico | 23.0 °C | 235 MPa Show Material materials with Límite elástico of 235 MPa | |
Módulo elástico | 23.0 °C | 150 GPa Show Material materials with Módulo elástico of 150 GPa | Typical for Nickel Chromium Iron Alloy |
Resistencia a la tracción | 23.0 °C | 430 MPa Show Material materials with Resistencia a la tracción of 430 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 285 - 545 J/(kg·K) Show Material materials with Calor específico of 285 - 545 J/(kg·K) | Typical for Nickel Chromium Iron Alloy |
Coeficiente de dilatación térmica | 23.0 °C | 7.6E-6 - 1.7E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 7.6E-6 - 1.7E-5 1/K | Typical for Nickel Chromium Iron Alloy |
Conductividad térmica | 23.0 °C | 8 - 35 W/(m·K) Show Material materials with Conductividad térmica of 8 - 35 W/(m·K) | Typical for Nickel Chromium Iron Alloy |
Temperatura de fusión | 1200 - 1480 °C Show Material materials with Temperatura de fusión of 1200 - 1480 °C | Typical for Nickel Chromium Iron Alloy |
Chemical properties
Property | Value |
---|---|
Azufre | 0.04 % Show Material materials with Azufre of 0.04 % |
Carbono | 0.35 - 0.75 % Show Material materials with Carbono of 0.35 - 0.75 % |
Cromo | 24 - 28 % Show Material materials with Cromo of 24 - 28 % |
Fósforo | 0.04 % Show Material materials with Fósforo of 0.04 % |
Manganeso | 2 % Show Material materials with Manganeso of 2 % |
Molibdeno | 0.5 % Show Material materials with Molibdeno of 0.5 % |
Níquel | 33 - 37 % Show Material materials with Níquel of 33 - 37 % |
Silicona | 2.5 % Show Material materials with Silicona of 2.5 % |