EN 10277-2 Grade S355J2G3C cold drawn

Want to keep this datasheet? Save it now in your required format

Description

S255J2G3C is used for folding, cold forming and cold drawing grade. The high-tensile fine grained steel is applicated for welding constructions of dynamic load at temperatures up to -20 °C. Compared to S235J2G3C is achievable a considerable material saving due to its by 120 MPa higher yield point. The steel shows compared to S235J2G3 a by 15% higher resistance to mineral sliding wear. Max. product thickness accounts 20 mm for folding grades and 8 mm for cold forming grades. As a bright steel product it is used in the form of bars, bright, straight, in various conditions (see DIN EN 10277 : 1999-10).

Related Standards

EN 10277-2

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value
Densidad	20.0 °C	7.85 g/cm³ Show Material materials with Densidad of 7.85 g/cm³

Mecánica

Property	Temperature	Value	Comment
Coeficiente de Poisson	23.0 °C	0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-]	Typical for Low Carbon Steel
Elongación	20.0 °C	6 - 9 % Show Material materials with Elongación of 6 - 9 %
Límite elástico Rp 0,2	20.0 °C	315 - 520 MPa Show Material materials with Límite elástico Rp 0,2 of 315 - 520 MPa
Módulo de cizallamiento	20.0 °C	81 GPa Show Material materials with Módulo de cizallamiento of 81 GPa
Módulo elástico	20.0 °C	210 GPa Show Material materials with Módulo elástico of 210 GPa
	100.0 °C	205 GPa Show Material materials with Módulo elástico of 205 GPa
	200.0 °C	195 GPa Show Material materials with Módulo elástico of 195 GPa
	300.0 °C	185 GPa Show Material materials with Módulo elástico of 185 GPa
	400.0 °C	175 GPa Show Material materials with Módulo elástico of 175 GPa

Resistencia a la tracción	20.0 °C	490 - 950 MPa Show Material materials with Resistencia a la tracción of 490 - 950 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	20.0 °C	450 J/(kg·K) Show Material materials with Calor específico of 450 J/(kg·K)
Coeficiente de dilatación térmica	100.0 °C	1.11E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.11E-5 1/K
	200.0 °C	1.21E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.21E-5 1/K
	300.0 °C	1.29E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.29E-5 1/K
	400.0 °C	1.35E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.35E-5 1/K
	Unlock all property charts
Conductividad térmica	20.0 °C	54 W/(m·K) Show Material materials with Conductividad térmica of 54 W/(m·K)
	100.0 °C	50.7 W/(m·K) Show Material materials with Conductividad térmica of 50.7 W/(m·K)
	200.0 °C	46.9 W/(m·K) Show Material materials with Conductividad térmica of 46.9 W/(m·K)
	300.0 °C	41.5 W/(m·K) Show Material materials with Conductividad térmica of 41.5 W/(m·K)
	400.0 °C	39.4 W/(m·K) Show Material materials with Conductividad térmica of 39.4 W/(m·K)
	Unlock all property charts
Temperatura de fusión		1480 - 1526 °C Show Material materials with Temperatura de fusión of 1480 - 1526 °C	Typical for Low Carbon Steel
Temperatura máx. de funcionamiento		500 °C Show Material materials with Temperatura máx. de funcionamiento of 500 °C	Typical for Carbon Steel
Temperatura máx. de funcionamiento, largo		-20 - 0 °C Show Material materials with Temperatura máx. de funcionamiento, largo of -20 - 0 °C

Eléctrico

Property	Temperature	Value
Resistividad eléctrica	20.0 °C	2E-7 Ω·m Show Material materials with Resistividad eléctrica of 2E-7 Ω·m

Magnético

Property	Value	Comment
Temperatura de Curie	770 °C Show Material materials with Temperatura de Curie of 770 °C	Typical for Low Carbon Steel

Chemical properties

Property	Value
Azufre	0.035 % Show Material materials with Azufre of 0.035 %
Carbono	0.2 % Show Material materials with Carbono of 0.2 %
Fósforo	0.04 % Show Material materials with Fósforo of 0.04 %
Manganeso	1.6 % Show Material materials with Manganeso of 1.6 %
Silicona	0.55 % Show Material materials with Silicona of 0.55 %