EN 12513 Grade GJN-HV600(XCr14)

Want to keep this datasheet? Save it now in your required format

Description

EN-GJN-HV600(XCr14) is a cast iron with a structure consisting of complex carbides. In the tempered conditions the matrix is mostly martensitic with partially austenite or other austenitic modifications. The material is comparable with DIN-materials G-X 300CrMo 15 3 and G-X 300 CrMoNi 15 2 1 acc. DIN 1695 : 1981-09 (invalid). Acc. to DIN: the materials are characterised by a high wear resistance and higher impact strength. The wear resistance increases with the carbon content, while the impact strength decreases. The machinability of material under annealed conditions depends on the carbon content. The material has a good hardening behaviour (G-X 300 CrMoNi 15 2 1). Cast parts made of cast iron with a high content on chromium are delivered under unfinished casting or heat treated conditions.

Related Standards

EN 12513

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Propiedades

General

Property	Temperature	Value	Comment
Densidad	23.0 °C	7.6 - 7.77 g/cm³ Show Material materials with Densidad of 7.6 - 7.77 g/cm³	Typical for White Cast Iron

Mecánica

Property	Temperature	Value	Comment
Coeficiente de Poisson	23.0 °C	0.27 [-] Show Material materials with Coeficiente de Poisson of 0.27 [-]	Typical for Cast Iron
Dureza Vickers	20.0 °C	600 [-] Show Material materials with Dureza Vickers of 600 [-]
Módulo de cizallamiento	23.0 °C	41 GPa Show Material materials with Módulo de cizallamiento of 41 GPa	Typical for Cast Iron
Módulo elástico	23.0 °C	165 - 240 GPa Show Material materials with Módulo elástico of 165 - 240 GPa	Typical for White Cast Iron

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	460 J/(kg·K) Show Material materials with Calor específico of 460 J/(kg·K)	Typical for White Cast Iron
Coeficiente de dilatación térmica	23.0 °C	1.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.5E-5 1/K	Typical for White Cast Iron
Conductividad térmica	23.0 °C	22 - 30 W/(m·K) Show Material materials with Conductividad térmica of 22 - 30 W/(m·K)	Typical for White Cast Iron
Temperatura de fusión		1209 °C Show Material materials with Temperatura de fusión of 1209 °C	Typical for White Cast Iron

Chemical properties

Property	Value
Azufre	0.08 % Show Material materials with Azufre of 0.08 %
Carbono	1.8 - 3.6 % Show Material materials with Carbono of 1.8 - 3.6 %
Cobre	1.2 % Show Material materials with Cobre of 1.2 %
Cromo	14 - 18 % Show Material materials with Cromo of 14 - 18 %
Fósforo	0.08 % Show Material materials with Fósforo of 0.08 %
Manganeso	0.5 - 1.5 % Show Material materials with Manganeso of 0.5 - 1.5 %
Molibdeno	3 % Show Material materials with Molibdeno of 3 %
Níquel	2 % Show Material materials with Níquel of 2 %
Silicona	1 % Show Material materials with Silicona of 1 %