EN 12165 Grade CuZn40Mn2Fe1 H080

Want to keep this datasheet? Save it now in your required format

Description

CuZn40Mn2Fe1(former identification: CuZn40Mn2) is an unhardenable copper alloy. High hardness and strength parameter are achievable by cold forming only. Tensile strength and Brinell hardness are higher than at CuZn31Si1 (CW708R). Manganese increases corrosion resistance and sliding qualities. CuZn40Mn2Fe1is weathering and seawater resistant. Processing properties: warm forming: good cold forming: moderately machinability: moderately hard soldering: good soft soldering: very good TIG-welding: moderately burnishing: very good Application in apparatus and general machine engineering, for fittings and refrigerators and for shock-absorber rods. In construction trade for weathering facades, for ornamental iron parts such as iron bars, gates or crosses.

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Propiedades

Mecánica

Property	Temperature	Value	Comment
Dureza Brinell	20.0 °C	80 [-] Show Material materials with Dureza Brinell of 80 [-]
Dureza Vickers	20.0 °C	85 [-] Show Material materials with Dureza Vickers of 85 [-]
Elongación	20.0 °C	15 % Show Material materials with Elongación of 15 %
Límite elástico Rp 0,2	20.0 °C	160 MPa Show Material materials with Límite elástico Rp 0,2 of 160 MPa
Módulo de cizallamiento	23.0 °C	40 GPa Show Material materials with Módulo de cizallamiento of 40 GPa	Typical for Wrought Copper Brass
Módulo elástico	23.0 °C	100 - 125 GPa Show Material materials with Módulo elástico of 100 - 125 GPa	Typical for Wrought Copper Brass
Resistencia a la tracción	20.0 °C	350 MPa Show Material materials with Resistencia a la tracción of 350 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	371 - 418 J/(kg·K) Show Material materials with Calor específico of 371 - 418 J/(kg·K)	Typical for Wrought Copper Brass
Coeficiente de dilatación térmica	23.0 °C	1.7E-5 - 2.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Conductividad térmica	23.0 °C	100 - 234 W/(m·K) Show Material materials with Conductividad térmica of 100 - 234 W/(m·K)	Typical for Wrought Copper Brass
Temperatura de fusión		875 - 1075 °C Show Material materials with Temperatura de fusión of 875 - 1075 °C	Typical for Wrought Copper Brass

Chemical properties

Property	Value
Aluminio	0.1 % Show Material materials with Aluminio of 0.1 %
Cobre	57 - 59 % Show Material materials with Cobre of 57 - 59 %
Estaño	0.5 % Show Material materials with Estaño of 0.5 %
Hierro	1.5 % Show Material materials with Hierro of 1.5 %
Manganeso	1 - 2.5 % Show Material materials with Manganeso of 1 - 2.5 %
Níquel	1 % Show Material materials with Níquel of 1 %
Plomo	0.8 % Show Material materials with Plomo of 0.8 %
Silicona	0.1 % Show Material materials with Silicona of 0.1 %