EN 12166 Grade CuZn10 H02

Want to keep this datasheet? Save it now in your required format

Description

CuZn10 (CW501L) is an unhardenable wrought alloy. High hardness and strength parameter are achievable by cold forming only. Thermal conductivity is lower than for CuZn5. Favorable electrical conductivity. Corrosion resistance is similar to pure copper. Processing properties: warm forming: moderately cold forming: good machinability: unfavorable hard and soft soldering: very good TIG-welding: good burnishing: good CuZn10 is used in electrical engineering, for metal goods as well as in jewelry and watches industry, for projectile casings and as cladding and enamelling material. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Related Standards

Equivalent Materials

Los datos sobre este material han sido proporcionados por WIAM.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Lectura sugerida

Properties of Copper

Do you supply similar materials?

List your company on Matmatch now and reach engineers around the world looking for such materials.

Request more information

Propiedades

Mecánica

Property	Temperature	Value	Comment
Dureza Vickers	20.0 °C	120 - 165 [-] Show Material materials with Dureza Vickers of 120 - 165 [-]
Límite elástico Rp 0,2	20.0 °C	350 - 390 MPa Show Material materials with Límite elástico Rp 0,2 of 350 - 390 MPa
Módulo de cizallamiento	23.0 °C	40 GPa Show Material materials with Módulo de cizallamiento of 40 GPa	Typical for Wrought Copper Brass
Módulo elástico	23.0 °C	100 - 125 GPa Show Material materials with Módulo elástico of 100 - 125 GPa	Typical for Wrought Copper Brass
Resistencia a la tracción	20.0 °C	410 - 570 MPa Show Material materials with Resistencia a la tracción of 410 - 570 MPa

Aplicaciones térmicas

Property	Temperature	Value	Comment
Calor específico	23.0 °C	371 - 418 J/(kg·K) Show Material materials with Calor específico of 371 - 418 J/(kg·K)	Typical for Wrought Copper Brass
Coeficiente de dilatación térmica	23.0 °C	1.7E-5 - 2.1E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.7E-5 - 2.1E-5 1/K	Typical for Wrought Copper Brass
Conductividad térmica	23.0 °C	100 - 234 W/(m·K) Show Material materials with Conductividad térmica of 100 - 234 W/(m·K)	Typical for Wrought Copper Brass
Temperatura de fusión		875 - 1075 °C Show Material materials with Temperatura de fusión of 875 - 1075 °C	Typical for Wrought Copper Brass

Chemical properties

Property	Value
Aluminio	0.02 % Show Material materials with Aluminio of 0.02 %
Cobre	89 - 91 % Show Material materials with Cobre of 89 - 91 %
Estaño	0.1 % Show Material materials with Estaño of 0.1 %
Hierro	0.05 % Show Material materials with Hierro of 0.05 %
Níquel	0.3 % Show Material materials with Níquel of 0.3 %
Plomo	0.05 % Show Material materials with Plomo of 0.05 %

Looking for suppliers of this material? Click to see 16 supplier of EN 12166 Grade CuZn10 H02 on Matmatch