General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 8.36 - 8.8 g/cm³ Show Material materials with Densidad of 8.36 - 8.8 g/cm³ |
Medidas
Property | Value | Comment |
---|---|---|
Diámetro | 0.76 - 63.5 mm Show Material materials with Diámetro of 0.76 - 63.5 mm | Smaller diameter wire may be produced by wire redrawers. |
Longitud | 3700 mm Show Material materials with Longitud of 3700 mm |
Mecánica
Property | Temperature | Value |
---|---|---|
Elongación | 23.0 °C | 2 - 75 % Show Material materials with Elongación of 2 - 75 % |
Límite elástico | 23.0 °C | 1220 MPa Show Material materials with Límite elástico of 1220 MPa |
Límite elástico Rp 0,2 | 23.0 °C | 130 - 1380 MPa Show Material materials with Límite elástico Rp 0,2 of 130 - 1380 MPa |
Módulo elástico | 23.0 °C | 120 - 131 GPa Show Material materials with Módulo elástico of 120 - 131 GPa |
Resistencia a la tracción | 23.0 °C | 410 - 1550 MPa Show Material materials with Resistencia a la tracción of 410 - 1550 MPa |
Aplicaciones térmicas
Property | Temperature | Value |
---|---|---|
Calor específico | 23.0 °C | 410 J/(kg·K) Show Material materials with Calor específico of 410 J/(kg·K) |
Coeficiente de dilatación térmica | 23.0 °C | 1.6E-5 - 1.75E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.6E-5 - 1.75E-5 1/K |
Conductividad térmica | 23.0 °C | 105 - 110 W/(m·K) Show Material materials with Conductividad térmica of 105 - 110 W/(m·K) |
Temperatura de fusión | 870 °C Show Material materials with Temperatura de fusión of 870 °C |
Eléctrico
Property | Temperature | Value |
---|---|---|
Resistividad eléctrica | 23.0 °C | 5.8E-6 - 7.8E-6 Ω·m Show Material materials with Resistividad eléctrica of 5.8E-6 - 7.8E-6 Ω·m |
Specific Electrical conductivity | 22 - 30 % IACS Show Material materials with Specific Electrical conductivity of 22 - 30 % IACS |
Chemical properties
Property | Value | Comment |
---|---|---|
Aluminio | 0 - 0.2 % Show Material materials with Aluminio of 0 - 0.2 % | |
Berilio | 1.8 - 2 % Show Material materials with Berilio of 1.8 - 2 % | |
Cobalto | 0.2 % Show Material materials with Cobalto of 0.2 % | min. Nickel + Cobalt |
Cobre | 95.5 - 97.8 % Show Material materials with Cobre of 95.5 - 97.8 % | Balance |
Hierro | 0 - 0.6 % Show Material materials with Hierro of 0 - 0.6 % | max., Nickel + Cobalt + Iron |
Níquel | 0.2 - 0.6 % Show Material materials with Níquel of 0.2 - 0.6 % | min. Nickel + Cobalt |
Otro | 0 - 0.5 % Show Material materials with Otro of 0 - 0.5 % | |
Plomo | 0.2 - 2 % Show Material materials with Plomo of 0.2 - 2 % | |
Silicona | 0 - 0.2 % Show Material materials with Silicona of 0 - 0.2 % |
Technological properties
Property | ||
---|---|---|
Application areas | Coaxial RF connectors and circular connectors and contact probes. This alloy to be fabricated into contacts for electronics, aircraft and automotive applications.,Contacts for electronics, aircraft and automotive applications. It can also be machined into parts for the watch industry, contacts for circular connectors and coaxial connectors. | |
General machinability | 60% (vs. free-cutting brass) |