Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Densidad | 23.0 °C | 8.83 - 8.9 g/cm³ Show Material materials with Densidad of 8.83 - 8.9 g/cm³ |
Medidas
| Property | Value | Comment | |
|---|---|---|---|
Ancho | 305 - 559 mm Show Material materials with Ancho of 305 - 559 mm | ||
Diámetro | 1.27 - 12.7 mm Show Material materials with Diámetro of 1.27 - 12.7 mm | ||
Diámetro exterior | 0.76 - 76 mm Show Material materials with Diámetro exterior of 0.76 - 76 mm | Rod | |
Espesor | 0.76 - 76 mm Show Material materials with Espesor of 0.76 - 76 mm | max.,Bar | |
Longitud | 610 - 91000 mm Show Material materials with Longitud of 610 - 91000 mm | max. Rod and Bar | |
Wall thickness | Typically 10 to 20% of OD | ||
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dureza Rockwell B | 23.0 °C | 92 [-] Show Material materials with Dureza Rockwell B of 92 [-] | |
Elongación | 20.0 °C | 15 % Show Material materials with Elongación of 15 % | min. |
23.0 °C | 5 - 25 % Show Material materials with Elongación of 5 - 25 % | min. | |
427.0 °C | 5 % Show Material materials with Elongación of 5 % | min. | |
Límite elástico | 23.0 °C | 760 MPa Show Material materials with Límite elástico of 760 MPa | |
Límite elástico Rp 0,2 | 20.0 °C | 585 MPa Show Material materials with Límite elástico Rp 0,2 of 585 MPa | |
23.0 °C | 650 - 870 MPa Show Material materials with Límite elástico Rp 0,2 of 650 - 870 MPa | ||
427.0 °C | 450 MPa Show Material materials with Límite elástico Rp 0,2 of 450 MPa | ||
Módulo elástico | 23.0 °C | 138 - 140 GPa Show Material materials with Módulo elástico of 138 - 140 GPa | |
Resistencia a la tracción | 20.0 °C | 690 MPa Show Material materials with Resistencia a la tracción of 690 MPa | |
23.0 °C | 750 - 970 MPa Show Material materials with Resistencia a la tracción of 750 - 970 MPa | ||
427.0 °C | 515 MPa Show Material materials with Resistencia a la tracción of 515 MPa | ||
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Calor específico | 23.0 °C | 340 - 414 J/(kg·K) Show Material materials with Calor específico of 340 - 414 J/(kg·K) | at 25°C |
Coeficiente de dilatación térmica | 23.0 °C | 1.76E-5 - 1.8E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.76E-5 - 1.8E-5 1/K | |
Conductividad térmica | 23.0 °C | 200 - 225 W/(m·K) Show Material materials with Conductividad térmica of 200 - 225 W/(m·K) | at 25°C |
Temperatura de fusión | 1010 - 1020 °C Show Material materials with Temperatura de fusión of 1010 - 1020 °C |
Eléctrico
| Property | Temperature | Value |
|---|---|---|
Resistividad eléctrica | 23.0 °C | 2.6E-6 - 3.8E-6 Ω·m Show Material materials with Resistividad eléctrica of 2.6E-6 - 3.8E-6 Ω·m |
Specific Electrical conductivity | 45 - 60 % IACS Show Material materials with Specific Electrical conductivity of 45 - 60 % IACS |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminio | 0 - 0.2 % Show Material materials with Aluminio of 0 - 0.2 % | |
Berilio | 0.4 - 0.7 % Show Material materials with Berilio of 0.4 - 0.7 % | |
Circonio | 0.12 - 0.4 % Show Material materials with Circonio of 0.12 - 0.4 % | |
Cobalto | 2 - 2.7 % Show Material materials with Cobalto of 2 - 2.7 % | |
Cobre | 95.6 - 97.2 % Show Material materials with Cobre of 95.6 - 97.2 % | Balance |
Hierro | 0 - 0.1 % Show Material materials with Hierro of 0 - 0.1 % | |
Otro | 0 - 0.5 % Show Material materials with Otro of 0 - 0.5 % | |
Silicona | 0 - 0.2 % Show Material materials with Silicona of 0 - 0.2 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | High performance powertrain automotive applications such as exhaust valve seats.,Typical applications include resistance welding components, and inserts for metal die casting, injection molding and blow molding.,Typical applications include dies casting plunger tips and dies for steel extrusion.,Typical applications include heat exchanger tubing and resistance welding components.,Typical applications include coil springs and formed wire contacts. | |