General
Property | Temperature | Value |
---|---|---|
Densidad | 23.0 °C | 2 g/cm³ Show Material materials with Densidad of 2 g/cm³ |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.29 [-] Show Material materials with Coeficiente de Poisson of 0.29 [-] | Typical for Magnesium |
Elongación | 23.0 °C | 2.1 % Show Material materials with Elongación of 2.1 % | |
Límite elástico | 23.0 °C | 140 MPa Show Material materials with Límite elástico of 140 MPa | |
Módulo de cizallamiento | 23.0 °C | 45 GPa Show Material materials with Módulo de cizallamiento of 45 GPa | Typical for Magnesium |
Módulo elástico | 23.0 °C | 49 GPa Show Material materials with Módulo elástico of 49 GPa | |
Resistencia a la tracción | 23.0 °C | 270 MPa Show Material materials with Resistencia a la tracción of 270 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 980 J/(kg·K) Show Material materials with Calor específico of 980 J/(kg·K) | |
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | |
Conductividad térmica | 23.0 °C | 153 - 167 W/(m·K) Show Material materials with Conductividad térmica of 153 - 167 W/(m·K) | Typical for Magnesium |
Temperatura de fusión | 440 °C Show Material materials with Temperatura de fusión of 440 °C |
Chemical properties
Property | Value |
---|---|
Aluminio | 8.3 - 9.7 % Show Material materials with Aluminio of 8.3 - 9.7 % |
Cobre | 0 - 0.25 % Show Material materials with Cobre of 0 - 0.25 % |
Magnesio | 86.7 - 90 % Show Material materials with Magnesio of 86.7 - 90 % |
Manganeso | 0.1 - 0.35 % Show Material materials with Manganeso of 0.1 - 0.35 % |
Níquel | 0 - 0.01 % Show Material materials with Níquel of 0 - 0.01 % |
Otro | 0 - 0.3 % Show Material materials with Otro of 0 - 0.3 % |
Silicona | 0 - 0.3 % Show Material materials with Silicona of 0 - 0.3 % |
Zinc | 1.6 - 2.4 % Show Material materials with Zinc of 1.6 - 2.4 % |