Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.06 % Show Supplier Material materials with Absorción de agua of 0.06 % | ISO 62-1 | (23°C/24hrs) |
Densidad | 23.0 °C | 1.69 g/cm³ Show Supplier Material materials with Densidad of 1.69 g/cm³ | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 0.8 % Show Supplier Material materials with Elongación of 0.8 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 21 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 21 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 235 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 235 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 12 GPa Show Supplier Material materials with Módulo de flexión of 12 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 13 GPa Show Supplier Material materials with Módulo elástico of 13 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 128 MPa Show Supplier Material materials with Resistencia a la flexión of 128 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 78 MPa Show Supplier Material materials with Resistencia a la tracción of 78 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 3 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 16 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 16 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3.08E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3.08E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.25E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.25E-5 1/K | ASTM E 831 | 40°C to 120°C | ||
Conductividad térmica | 23.0 °C | 3.3 W/(m·K) Show Supplier Material materials with Conductividad térmica of 3.3 W/(m·K) | ISO 22007-2 | 60*60*3mm plaque | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 162 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 162 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Temperatura de flexión bajo carga | 162 - 204 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 162 - 204 °C | ||||
Thermal conductivity, through-plane | 23.0 °C | 1 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 1 W/(m·K) | ISO 22007-2 | 60*60*3mm plaque | ||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101694795- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.8mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 800°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dielectric constant, 1GHz | 23.0 °C | 4.86 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 4.86 [-] | ASTM ES 7-83 | 1.1 GHz |
Dissipation factor, 1GHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 0.01 [-] | ASTM ES 7-83 | |
High Amp Arc Ignition | 23.0 °C | 0.8 mm Show Supplier Material materials with High Amp Arc Ignition of 0.8 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 0.8 mm Show Supplier Material materials with Hot-Wire Ignition of 0.8 mm | ≥, UL 746A | PLC 1 |
Rigidez dieléctrica | 23.0 °C | 10 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 10 kV/mm | >, ASTM D 149 | in oil, 1.0 mm |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 | |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | LED Lighting, Electronic Components | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |