Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.23 % Show Supplier Material materials with Absorción de agua of 0.23 % | ISO 62-1 | (23°C/24hrs) |
Densidad | 23.0 °C | 1.68 g/cm³ Show Supplier Material materials with Densidad of 1.68 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.1 % Show Supplier Material materials with Elongación of 1.1 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 15 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 15 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 152 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 152 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 12 GPa Show Supplier Material materials with Módulo de flexión of 12 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 13 GPa Show Supplier Material materials with Módulo elástico of 13 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 105 MPa Show Supplier Material materials with Resistencia a la flexión of 105 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 75 MPa Show Supplier Material materials with Resistencia a la tracción of 75 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 3 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 9 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 165°C +/- 2°C | |||
Coeficiente de dilatación térmica | 23.0 °C | 3.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3.9E-5 1/K | ISO 11359-2 | -30°C to 80°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.5E-5 1/K | ISO 11359-2 | -30°C to 80°C | ||
Conductividad térmica | 23.0 °C | 5.5 W/(m·K) Show Supplier Material materials with Conductividad térmica of 5.5 W/(m·K) | ISO 22007-2 | 60*60*3mm plaque | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 800 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 800 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 203 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 160 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 160 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 100 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 100 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Temperatura de flexión bajo carga | 160 - 203 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 160 - 203 °C | ||||
Thermal conductivity, through-plane | 23.0 °C | 1.2 W/(m·K) Show Supplier Material materials with Thermal conductivity, through-plane of 1.2 W/(m·K) | ISO 22007-2 | 60*60*3mm plaque | ||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101769086- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.8mm UL 94 <br> Glow Wire Flammability Index, 0.8 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.6 mm: 960°C IEC 60695-2-12 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 0.8 mm Show Supplier Material materials with High Amp Arc Ignition of 0.8 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 0.8 mm Show Supplier Material materials with Hot-Wire Ignition of 0.8 mm | ≥, UL 746A | PLC 0 |
Rigidez dieléctrica | 23.0 °C | 6.1 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 6.1 kV/mm | IEC 60243-1 | 1.6 mm |
Sheet resistivity, ROA | 23.0 °C | 4.00E+14 Ω Show Supplier Material materials with Sheet resistivity, ROA of 4.00E+14 Ω | ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Supplier Material materials with Índice de seguimiento comparativo of 0 V | UL 746A | (UL) {PLC} |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | LED Lighting | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |