Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.4 [-] | ASTM E 132 |
Elongación | 23.0 °C | 1.1 % Show Supplier Material materials with Elongación of 1.1 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 82 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 82 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 713 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 713 J/m | ASTM D 4812 | 23°C |
Módulo de cizallamiento | 23.0 °C | 4.7 GPa Show Supplier Material materials with Módulo de cizallamiento of 4.7 GPa | ASTM D732 |
Módulo de flexión | 23.0 °C | 23.9 GPa Show Supplier Material materials with Módulo de flexión of 23.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 29.3 GPa Show Supplier Material materials with Módulo elástico of 29.3 GPa | ISO 527 | 1 mm/min |
Resistencia a la compresión | 23.0 °C | 231 MPa Show Supplier Material materials with Resistencia a la compresión of 231 MPa | SABIC method |
Resistencia a la flexión | 23.0 °C | 332 MPa Show Supplier Material materials with Resistencia a la flexión of 332 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 252 MPa Show Supplier Material materials with Resistencia a la tracción of 252 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 82 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 82 kJ/m² | ASTM D 256 | notched, 23°C |
Resistencia al cizallamiento | 23.0 °C | 128 MPa Show Supplier Material materials with Resistencia al cizallamiento of 128 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5E-6 1/K | ASTM E 831 | -40°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7E-6 1/K | ASTM E 831 | -40°C to 150°C |
Heat deflection temperature, 1.80 MPa | 195 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 195 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 195 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 195 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | ASTM D 955 | 24 hrs |
Contracción transversal | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción transversal of 0.1 % | ASTM D 955 | 24 hrs |
Velocidad de flujo de la masa derretida | 69 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 69 g/10min | ASTM D 1238 | 380°C/6.7 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Air Cabin Interiors, Aircraft Seating | |
Availability | Europe,Asia,Americas | |
Processing methods | Maximum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |