FLEX NORYL™ Resin WCV063 - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCV063 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 63. FLEX NORYL WCV063 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Ingeniería eléctrica

Automotriz

Piezas generales para vehículos

Automotive Interior

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Densidad relativa	23.0 °C	1.03 [-] Show Supplier Material materials with Densidad relativa of 1.03 [-]	ASTM D 792

Mecánica

Property	Temperature	Value	Comment
Dureza Shore D	23.0 °C	63 [-] Show Supplier Material materials with Dureza Shore D of 63 [-]	ASTM D 2240 \| 10S reading
Elongación	23.0 °C	50 % Show Supplier Material materials with Elongación of 50 %	ISO 527 \| break, 50 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	170 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 170 J/m	ASTM D 256 \| notched, -30°C
Módulo de flexión	23.0 °C	0.8 GPa Show Supplier Material materials with Módulo de flexión of 0.8 GPa	ISO 178
Módulo elástico	23.0 °C	0.7 GPa Show Supplier Material materials with Módulo elástico of 0.7 GPa	ISO 527 \| 1 mm/min
Resistencia a la tracción	23.0 °C	25 MPa Show Supplier Material materials with Resistencia a la tracción of 25 MPa	ISO 527 \| yield
Resistencia al choque, ensayo Izod entallado	23.0 °C	37 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 37 kJ/m²	ISO 180/1A \| 80104, 23°C

Aplicaciones térmicas

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	82 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 82 °C	ASTM D 648 \| 3.2 mm, unannealed
Heat deflection temperature, 1.80 MPa	66 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 66 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Temperatura de flexión bajo carga	66 - 82 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 66 - 82 °C

Eléctrico

Property	Temperature	Value	Comment
Dielectric constant, 1GHz	23.0 °C	2.47 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 2.47 [-]	ASTM D 150
Dissipation factor, 1GHz	23.0 °C	3.2E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 3.2E-3 [-]	ASTM D 150

Rheological Properties

Property	Value	Comment
Velocidad de flujo de la masa derretida	33 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 33 g/10min	ASTM D 1238 \| 280°C/5.0 kgf

Technological properties

Property
Application areas	Airbag, Auto Electrical, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 80 to 100.0°C Die Temperature: 280 to 300.0°C Extruder Length/Diameter Ratio (L/D): >24:1- Drying Time (Cumulative): 8hrs Neck Temperature: 280 to 300.0°C Melt Temperature: 280 to 300.0°C Drying Time: 4 to 6.0hrs Middle Zone Temperatures: 270 to 300.0°C Cooling Water Air Gap: 100 to 1000.0mm Conductor Pre-heat Temperature: 100 to 150.0°C Screw Speed: 5 to 60.0rpm Water Bath Temperature: 15 to 30.0°C Maximum Moisture Content: 0.02% Cross-head Temperature: 280 to 300.0°C Head Zone Temperature: 280 to 300.0°C Feed Zone Temperature: 200 to 260.0°C Screen Pack: 60/200/60- Compression Ratio: 2:1-3:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.