General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 2.3 % Show Supplier Material materials with Absorción de agua of 2.3 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.31 g/cm³ Show Supplier Material materials with Densidad of 1.31 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.31 [-] Show Supplier Material materials with Densidad relativa of 1.31 [-] | ASTM D 792 | |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 7 % Show Supplier Material materials with Elongación of 7 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 43 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 43 J/m | ASTM D 256 |
Módulo de flexión | 23.0 °C | 2.9 GPa Show Supplier Material materials with Módulo de flexión of 2.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo elástico of 3.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 120 MPa Show Supplier Material materials with Resistencia a la flexión of 120 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 101 MPa Show Supplier Material materials with Resistencia a la tracción of 101 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.1E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Heat deflection temperature, 0.45 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 250 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 223 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 223 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 223 - 250 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 223 - 250 °C | ||
Temperatura de reblandecimiento Vicat | 247 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 247 °C | ISO 306 | Rate B/120 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.4 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.4 [-] | ASTM D 150 |
Dielectric constant, 1KHz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Dielectric constant, 1KHz of 3.5 [-] | ASTM D 150 |
Rigidez dieléctrica | 23.0 °C | 25 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 25 kV/mm | ASTM D 149 | in air, 1.6 mm |
Índice de seguimiento comparativo | 23.0 °C | 125 V Show Supplier Material materials with Índice de seguimiento comparativo of 125 V | IEC 60112 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1 % Show Supplier Material materials with Contracción of 1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 10 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 10 g/10min | ASTM D 1238 | 367°C/6.6 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Non-LED Lighting, Wireless Communications, Wearables, Circuit Protection, Data Transfer, Data Management, Electronic Components, Fluid Delivery | |
Availability | Europe,Asia,Americas | |
Processing methods | Mold Temperature: 160 to 200.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |