Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 100 % Show Supplier Material materials with Elongación of 100 % | ASTM D 638 | brk, Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 650 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 650 J/m | ASTM D 256 | -40°C |
Instrumented Impact, Total Energy | 23.0 °C | 70 J Show Supplier Material materials with Instrumented Impact, Total Energy of 70 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Supplier Material materials with Módulo de flexión of 2.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo elástico of 2.2 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 90 MPa Show Supplier Material materials with Resistencia a la flexión of 90 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 55 MPa Show Supplier Material materials with Resistencia a la tracción of 55 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 65 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 65 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 800 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 800 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 875 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 875 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 1.80 MPa | 123 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 123 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 123 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 123 °C | ||||
Temperatura de reblandecimiento Vicat | 145 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 145 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100656423- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 875°C IEC 60695-2-13 <br> Glow Wire Ignitability Temperature, 1.0 mm: 875°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 850°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.0 mm: 850°C IEC 60695-2-12 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 9.3E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 9.3E-3 [-] | ASTM D 150 | |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 3 |
Rigidez dieléctrica | 23.0 °C | 15 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 15 kV/mm | ASTM D 149 | in oil, 0.8 mm |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 10 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 10 g/10min | ASTM D 1238 | 300°C/1.2 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wireless Communications, Wearables, Photo/Video Camera, Personal Computing | |
| Availability | Europe,Asia | |
| Processing methods | Drying Temperature: 120°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |