General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.8 % Show Supplier Material materials with Absorción de agua of 0.8 % | ISO 62-1 | (23°C/saturated) |
Densidad relativa | 23.0 °C | 1.55 [-] Show Supplier Material materials with Densidad relativa of 1.55 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.15 % Show Supplier Material materials with Moisture absorption of 0.15 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.8 % Show Supplier Material materials with Elongación of 2.8 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 150 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 150 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 12 J Show Supplier Material materials with Instrumented Impact, Total Energy of 12 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 13 GPa Show Supplier Material materials with Módulo de flexión of 13 GPa | ASTM D 790 |
Módulo elástico | 23.0 °C | 15 GPa Show Supplier Material materials with Módulo elástico of 15 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 310 MPa Show Supplier Material materials with Resistencia a la flexión of 310 MPa | ASTM D 790 |
Resistencia a la tracción | 23.0 °C | 212 MPa Show Supplier Material materials with Resistencia a la tracción of 212 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 16 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 16 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 150 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 150 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ASTM D 648 | 3.2mm, unannealed | |
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |
Temperatura de flexión bajo carga | 250 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 250 °C | ||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101337256- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.8mm UL 94 |
Eléctrico
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.12 % Show Supplier Material materials with Contracción of 0.12 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.44 % Show Supplier Material materials with Contracción transversal of 0.44 % | SABIC method | 3.2 mm |
Velocidad de flujo del volumen derretido | 15 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 15 cm³/10min | ISO 1133 | MVR at 300°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |