Propiedades
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.7 % Show Supplier Material materials with Elongación of 1.7 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 43 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 43 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 370 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 370 J/m | ASTM D 4812 | 23°C |
Resistencia a la flexión | 23.0 °C | 148 MPa Show Supplier Material materials with Resistencia a la flexión of 148 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 96 MPa Show Supplier Material materials with Resistencia a la tracción of 96 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 2 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Value | Comment |
|---|---|---|
Heat deflection temperature, 1.80 MPa | 122 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 122 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Temperatura de flexión bajo carga | 122 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 122 °C |
Technological properties
| Property | ||
|---|---|---|
| Availability | Asia,Americas | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |