General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.2 % Show Supplier Material materials with Absorción de agua of 1.2 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.28 g/cm³ Show Supplier Material materials with Densidad of 1.28 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.28 [-] Show Supplier Material materials with Densidad relativa of 1.28 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.2 % Show Supplier Material materials with Moisture absorption of 0.2 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 50 % Show Supplier Material materials with Elongación of 50 % | ISO 527 | break, 5 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 59 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 59 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2100 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2100 J/m | ASTM D 4812 | 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 30 J Show Supplier Material materials with Instrumented Impact, Total Energy of 30 J | ASTM D 3763 | 23°C | ||
Módulo de flexión | 23.0 °C | 2.9 GPa Show Supplier Material materials with Módulo de flexión of 2.9 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.9 GPa Show Supplier Material materials with Módulo elástico of 2.9 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 110 MPa Show Supplier Material materials with Resistencia a la flexión of 110 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 85 MPa Show Supplier Material materials with Resistencia a la tracción of 85 MPa | ISO 527 | break, 5 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | 80*10*4, -30°C | ||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Izod no entallado | ISO 180/1U | unnotched 80*10*4 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Ball Pressure Test | Passes | IEC 60695-10-2 | 125°C +/- 2°C | |
Coeficiente de dilatación térmica | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.5E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.5E-5 1/K | ISO 11359-2 | 23°C to 150°C |
Conductividad térmica | 23.0 °C | 0.31 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.31 W/(m·K) | ASTM C177 |
Heat deflection temperature, 0.45 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 208 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 198 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 198 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 198 - 208 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 198 - 208 °C | ||
Temperatura de reblandecimiento Vicat | 220 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 220 °C | ISO 306 | Rate A/50 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 60Hz | 23.0 °C | 3.2 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.2 [-] | ASTM D 150 | 50/60 Hz |
Dissipation factor, 50Hz | 23.0 °C | 2.1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 2.1E-3 [-] | IEC 60250 | 50/60 Hz |
Rigidez dieléctrica | 23.0 °C | 18.1 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 18.1 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 2.50E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.50E+15 Ω·cm | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 150 V Show Supplier Material materials with Índice de seguimiento comparativo of 150 V | IEC 60112 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | SABIC method | on tensile bar |
Contracción transversal | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción transversal of 0.4 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 11 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 11 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Velocidad de flujo del volumen derretido | 20 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 20 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Air Cabin Interiors, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Middle - Zone 2 Temperature: 355 to 375.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |