Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.04 % Show Supplier Material materials with Absorción de agua of 0.04 % | ISO 62 |
Densidad | 23.0 °C | 1.38 g/cm³ Show Supplier Material materials with Densidad of 1.38 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.2 % Show Supplier Material materials with Elongación of 1.2 % | ISO 527 |
Módulo de flexión | 23.0 °C | 11 GPa Show Supplier Material materials with Módulo de flexión of 11 GPa | ISO 178 |
Resistencia a la flexión | 23.0 °C | 235 MPa Show Supplier Material materials with Resistencia a la flexión of 235 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 155 MPa Show Supplier Material materials with Resistencia a la tracción of 155 MPa | ISO 527 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 6 kJ/m² | ISO 179 |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Heat deflection temperature, 1.80 MPa | 255 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 255 °C | ISO 75 | |
Temperatura de fusión | 280 °C Show Supplier Material materials with Temperatura de fusión of 280 °C | ISO 11357 (10°C/min) | |
Temperatura máx. de funcionamiento | 255 °C Show Supplier Material materials with Temperatura máx. de funcionamiento of 255 °C | ||
Inflamabilidad | V-0, UL-94 | ||
Technological properties
| Property | ||
|---|---|---|
| Application areas | Can be produced Bearing seat, the aircraft shell, dashboard, universal head, sealing parts | |
| Fillers | 10% Carbon Fiber and PTFE | |
| Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min | |