General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.02 % Show Supplier Material materials with Absorción de agua of 0.02 % | ISO 62 |
Densidad | 23.0 °C | 1.67 g/cm³ Show Supplier Material materials with Densidad of 1.67 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.7 % Show Supplier Material materials with Elongación of 1.7 % | ISO 527 |
Módulo de flexión | 23.0 °C | 14 GPa Show Supplier Material materials with Módulo de flexión of 14 GPa | ISO 178 |
Resistencia a la flexión | 23.0 °C | 265 MPa Show Supplier Material materials with Resistencia a la flexión of 265 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 175 MPa Show Supplier Material materials with Resistencia a la tracción of 175 MPa | ISO 527 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179 |
Aplicaciones térmicas
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 4 [-] Show Supplier Material materials with Constante dieléctrica of 4 [-] | IEC 60250 |
Factor de disipación | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Factor de disipación of 2E-3 [-] | IEC 60250 |
Rigidez dieléctrica | 23.0 °C | 16 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 16 kV/mm | IEC 60243 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 150 V Show Supplier Material materials with Índice de seguimiento comparativo of 150 V | IEC 60112 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in electronics,communications,high-frequency heating industrial equipment and measurement, inspection and test equipment such as the need to engage in electrostatic and electromagnetic shielding and other occasions, in order to reduce the source magnetic radiation effect | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |