Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.6 % Show Supplier Material materials with Elongación of 1.6 % | ISO 527 |
Módulo de flexión | 23.0 °C | 15 GPa Show Supplier Material materials with Módulo de flexión of 15 GPa | ISO 178 |
Resistencia a la flexión | 23.0 °C | 250 MPa Show Supplier Material materials with Resistencia a la flexión of 250 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 165 MPa Show Supplier Material materials with Resistencia a la tracción of 165 MPa | ISO 527 |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179 |
Aplicaciones térmicas
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 4 [-] Show Supplier Material materials with Constante dieléctrica of 4 [-] | IEC 60250 |
Factor de disipación | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Factor de disipación of 2E-3 [-] | IEC 60250 |
Rigidez dieléctrica | 23.0 °C | 16 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 16 kV/mm | IEC 60243 |
Volume resistivity | 23.0 °C | 2.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 2.00E+15 Ω·cm | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 155 V Show Supplier Material materials with Índice de seguimiento comparativo of 155 V | IEC 60112 |
Technological properties
Property | ||
---|---|---|
Application areas | Can be used in electronics,communications,high-frequency heating industrial equipment and measurement, inspection and test equipment such as the need to engage in electrostatic and electromagnetic shielding and other occasions, in order to reduce the source magnetic radiation effect | |
Fillers | 40% Glass Fiber | |
Processing methods | Injection Moulding / Test Specimen Production: Drying: 150°C & 3 hours - Injection Pressure: 30-100 MPa - Injection Molding Melt Temperature: 290-330°C - Injection Molding Mold Temperature: 120-160°C - Limit in-cylinder Retention Time: 300°C/60min or 320°C/30min |