General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 20.0 °C | 4.55 g/cm³ Show Material materials with Densidad of 4.55 g/cm³ | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Elongación | 20.0 °C | 8.0 % Show Material materials with Elongación of 8.0 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Estricción | 20.0 °C | 20.0 % Show Material materials with Estricción of 20.0 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Módulo de cizallamiento | 20.0 °C | 43.0 GPa Show Material materials with Módulo de cizallamiento of 43.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Módulo elástico | 20.0 °C | 114.0 GPa Show Material materials with Módulo elástico of 114.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
200.0 °C | 104.0 GPa Show Material materials with Módulo elástico of 104.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging | |
400.0 °C | 93.0 GPa Show Material materials with Módulo elástico of 93.0 GPa | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging | |
Resistencia a la tracción | 20.0 °C | 890.0 MPa Show Material materials with Resistencia a la tracción of 890.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging |
20.0 °C | 920.0 MPa Show Material materials with Resistencia a la tracción of 920.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Rod | |
20.0 °C | 1030.0 MPa Show Material materials with Resistencia a la tracción of 1030.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
100.0 °C | 945.0 MPa Show Material materials with Resistencia a la tracción of 945.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
200.0 °C | 885.0 MPa Show Material materials with Resistencia a la tracción of 885.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
300.0 °C | 845.0 MPa Show Material materials with Resistencia a la tracción of 845.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
400.0 °C | 785.0 MPa Show Material materials with Resistencia a la tracción of 785.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | ||
500.0 °C | 735.0 MPa Show Material materials with Resistencia a la tracción of 735.0 MPa | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Calor específico | 370.0 - 674.0 J/(kg·K) Show Material materials with Calor específico of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Coeficiente de dilatación térmica | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Conductividad térmica | 20.0 °C | 5.86 W/(m·K) Show Material materials with Conductividad térmica of 5.86 W/(m·K) | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging | |
Temperatura de fusión | 1500.0 - 1750.0 °C Show Material materials with Temperatura de fusión of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy |
Eléctrico
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Resistividad eléctrica | 20.0 °C | 1.91e-06 Ω·m Show Material materials with Resistividad eléctrica of 1.91e-06 Ω·m | Artificially Aged | DIN 17851, DIN 17862, DIN 17864 | Forging |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminio | 5.5 - 6.5 % Show Material materials with Aluminio of 5.5 - 6.5 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Carbono | 0.05 Show Material materials with Carbono of 0.05 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Circonio | 3.6 - 4.4 % Show Material materials with Circonio of 3.6 - 4.4 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Estaño | 1.8 - 2.2 % Show Material materials with Estaño of 1.8 - 2.2 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Hidrógeno | 0.015 Show Material materials with Hidrógeno of 0.015 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Hierro | 0.25 Show Material materials with Hierro of 0.25 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Molibdeno | 1.8 - 2.2 % Show Material materials with Molibdeno of 1.8 - 2.2 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Nitrógeno | 0.05 Show Material materials with Nitrógeno of 0.05 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Oxígeno | 0.15 Show Material materials with Oxígeno of 0.15 | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Silicona | 0.06 - 0.12 % Show Material materials with Silicona of 0.06 - 0.12 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |
Titanio | 83.7 % Show Material materials with Titanio of 83.7 % | Artificially Aged | DIN 17851, DIN 17864, DIN 17862 | Forging, Rod |