General
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Densidad | 20.0 °C | 4.54 g/cm³ Show Material materials with Densidad of 4.54 g/cm³ | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Mecánica
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Módulo de cizallamiento | 20.0 °C | 45.0 GPa Show Material materials with Módulo de cizallamiento of 45.0 GPa | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Módulo elástico | 20.0 °C | 116.0 GPa Show Material materials with Módulo elástico of 116.0 GPa | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
200.0 °C | 108.0 GPa Show Material materials with Módulo elástico of 108.0 GPa | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | |
400.0 °C | 99.0 GPa Show Material materials with Módulo elástico of 99.0 GPa | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | |
Plane-Strain Fracture Toughnes | 20.0 °C | 46.9 - 49.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.9 - 49.6 MPa·√m | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
20.0 °C | 46.9 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 46.9 MPa·√m | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | |
20.0 °C | 49.6 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 49.6 MPa·√m | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Aplicaciones térmicas
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Calor específico | 370.0 - 674.0 J/(kg·K) Show Material materials with Calor específico of 370.0 - 674.0 J/(kg·K) | Typical for Titanium Alpha Beta Alloy | ||||
Coeficiente de dilatación térmica | 7.699999999999999e-06 - 1e-05 1/K Show Material materials with Coeficiente de dilatación térmica of 7.699999999999999e-06 - 1e-05 1/K | Typical for Titanium Alpha Beta Alloy | ||||
Conductividad térmica | 20.0 °C | 6.5 W/(m·K) Show Material materials with Conductividad térmica of 6.5 W/(m·K) | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging | |
Temperatura de fusión | 1500.0 - 1750.0 °C Show Material materials with Temperatura de fusión of 1500.0 - 1750.0 °C | Typical for Titanium Alpha Beta Alloy |
Eléctrico
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Resistividad eléctrica | 20.0 °C | 1.57e-06 Ω·m Show Material materials with Resistividad eléctrica of 1.57e-06 Ω·m | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminio | 5.0 - 6.0 % Show Material materials with Aluminio of 5.0 - 6.0 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Carbono | 0.05 Show Material materials with Carbono of 0.05 | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Cobre | 0.35 - 1.0 % Show Material materials with Cobre of 0.35 - 1.0 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Estaño | 1.5 - 2.5 % Show Material materials with Estaño of 1.5 - 2.5 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Hierro | 0.35 - 1.0 % Show Material materials with Hierro of 0.35 - 1.0 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Nitrógeno | 0.04 Show Material materials with Nitrógeno of 0.04 | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Oxígeno | 0.2 Show Material materials with Oxígeno of 0.2 | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Titanio | 82.8 % Show Material materials with Titanio of 82.8 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |
Vanadio | 5.0 - 6.0 % Show Material materials with Vanadio of 5.0 - 6.0 % | precipitation hardened (+P) | WL 3.7174-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860 | Rod, Forging |