General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 19.3 g/cm³ Show Material materials with Densidad of 19.3 g/cm³ | Typical for Gold |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.42 [-] Show Material materials with Coeficiente de Poisson of 0.42 [-] | Typical for Gold |
Dureza Vickers | 20.0 °C | 235 [-] Show Material materials with Dureza Vickers of 235 [-] | |
Elongación | 20.0 °C | 17 % Show Material materials with Elongación of 17 % | |
Límite elástico Rp 0,2 | 20.0 °C | 620 MPa Show Material materials with Límite elástico Rp 0,2 of 620 MPa | |
Módulo de cizallamiento | 23.0 °C | 26 GPa Show Material materials with Módulo de cizallamiento of 26 GPa | Typical for Gold |
Módulo elástico | 23.0 °C | 74 - 81 GPa Show Material materials with Módulo elástico of 74 - 81 GPa | Typical for Gold |
Resistencia a la tracción | 20.0 °C | 740 MPa Show Material materials with Resistencia a la tracción of 740 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 126 - 138 J/(kg·K) Show Material materials with Calor específico of 126 - 138 J/(kg·K) | Typical for Gold |
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | Typical for Gold |
Conductividad térmica | 23.0 °C | 292 - 316 W/(m·K) Show Material materials with Conductividad térmica of 292 - 316 W/(m·K) | Typical for Gold |
Temperatura de fusión | 1064 °C Show Material materials with Temperatura de fusión of 1064 °C | Typical for Gold |