General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 12.16 g/cm³ Show Material materials with Densidad of 12.16 g/cm³ | Typical for Palladium |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.39 [-] Show Material materials with Coeficiente de Poisson of 0.39 [-] | Typical for Palladium |
Dureza Vickers 5 | 20.0 °C | 160 [-] Show Material materials with Dureza Vickers 5 of 160 [-] | |
Elongación | 20.0 °C | 29 % Show Material materials with Elongación of 29 % | |
Límite elástico Rp 0,2 | 20.0 °C | 340 MPa Show Material materials with Límite elástico Rp 0,2 of 340 MPa | |
Módulo de cizallamiento | 23.0 °C | 42 GPa Show Material materials with Módulo de cizallamiento of 42 GPa | Typical for Palladium |
Módulo elástico | 23.0 °C | 121 GPa Show Material materials with Módulo elástico of 121 GPa | Typical for Palladium |
Resistencia a la tracción | 20.0 °C | 630 MPa Show Material materials with Resistencia a la tracción of 630 MPa |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 236 - 248 J/(kg·K) Show Material materials with Calor específico of 236 - 248 J/(kg·K) | Typical for Palladium |
Coeficiente de dilatación térmica | 23.0 °C | 1.1E-5 - 1.4E-5 1/K Show Material materials with Coeficiente de dilatación térmica of 1.1E-5 - 1.4E-5 1/K | Typical for Palladium |
Conductividad térmica | 23.0 °C | 60 - 76 W/(m·K) Show Material materials with Conductividad térmica of 60 - 76 W/(m·K) | Typical for Palladium |
Temperatura de fusión | 1553 °C Show Material materials with Temperatura de fusión of 1553 °C | Typical for Palladium |