General
Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³ | ASTM D 792 |
Limiting oxygen index | 23.0 °C | 25 % Show Supplier Material materials with Limiting oxygen index of 25 % | |
Relative density | 23.0 °C | 1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-] | ASTM D 792 |
Specific volume | 23.0 °C | 0.83 cm³/g Show Supplier Material materials with Specific volume of 0.83 cm³/g | ASTM D 792 |
Water absorption | 23.0 °C | 0.35 % Show Supplier Material materials with Water absorption of 0.35 % | ASTM D 570 | (23°C/Saturated) |
Mechanical
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elastic modulus | 23.0 °C | 2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa | ISO 527 | 1 mm/min | ||
Elongation | 23.0 °C | 70 % Show Supplier Material materials with Elongation of 70 % | ISO 527 | break, 50 mm/min | ||
Flexural modulus | 23.0 °C | 2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa | ISO 178 | 2 mm/min | ||
Flexural strength | 23.0 °C | 90 MPa Show Supplier Material materials with Flexural strength of 90 MPa | ISO 178 | yield, 2 mm/min | ||
Hardness, Rockwell M | 23.0 °C | 70 [-] Show Supplier Material materials with Hardness, Rockwell M of 70 [-] | ASTM D 785 | | ||
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 | ||
Impact strength, Charpy notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 12 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm | ||
Impact strength, Izod notched | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 640 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 640 J/m | ASTM D 256 | ||
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | 23°C | ||
Instrumented Impact, at Peak | 23.0 °C | 54 J Show Supplier Material materials with Instrumented Impact, at Peak of 54 J | ASTM D 3763 | 23°C | ||
Taber Abrasion | 23.0 °C | 10 mg/1000cy Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy | ASTM D 1044 | CS-17, 1 kg | ||
Tensile strength | 23.0 °C | 50 MPa Show Supplier Material materials with Tensile strength of 50 MPa | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod unnotched | ISO 180/1U | unnotched 80*10*4, -30°C |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature | 121 - 133 °C Show Supplier Material materials with Heat deflection temperature of 121 - 133 °C | ||||
Heat deflection temperature, 0.45 MPa | 133 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 133 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |||
Relative temperature index, mechanical impact | 130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |||
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |||
Specific heat capacity | 23.0 °C | 1.25E-3 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1.25E-3 J/(kg·K) | ASTM C 351 | ||
Thermal conductivity | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 145 °C Show Supplier Material materials with Vicat softening temperature of 145 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956751- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.1mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103876512- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 2 V Show Supplier Material materials with Comparative tracking index of 2 V | UL 746A | (UL) {PLC} |
Dielectric constant, 1MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.7 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.7 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 17 kV/mm Show Supplier Material materials with Dielectric strength of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1E-3 [-] | IEC 60250 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, IEC 60093 | |
Optical
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 25 g/10min Show Supplier Material materials with Melt mass-flow rate of 25 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Melt volume-flow rate | 23 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 23 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg | |
Shrinkage | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage of 0.5 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |