LEXAN™ Copolymer FXE141R

Want to keep this datasheet? Save it now in your required format

Description

Transparent PC. ILLUMINATE special effects (fluorescent/edge glow colors). MFR 10.1. Internal mold release.

This material data has been provided by Sabic.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Applications

Electronics

Display Devices

Automotive

General Automotive Parts

Automotive Interior

Construction

Lighting

Road Vehicle Systems

Car Lighting

Water Management

Defense

Show all

Materials by this supplier

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

See all materials by this supplier

Properties

General

Property	Temperature	Value	Comment
Density	23.0 °C	1.19 g/cm³ Show Supplier Material materials with Density of 1.19 g/cm³	ASTM D 792
Moisture absorption	23.0 °C	0.15 % Show Supplier Material materials with Moisture absorption of 0.15 %	ISO 62 \| (23°C / 50% RH)
Relative density	23.0 °C	1.2 [-] Show Supplier Material materials with Relative density of 1.2 [-]	ASTM D 792 \|
Specific volume	23.0 °C	0.83 cm³/g Show Supplier Material materials with Specific volume of 0.83 cm³/g	ASTM D 792
Water absorption	23.0 °C	0.35 % Show Supplier Material materials with Water absorption of 0.35 %	ISO 62-1 \| (23°C/saturated)

Mechanical

Property	Temperature	Value	Comment
Elastic modulus	23.0 °C	2.4 GPa Show Supplier Material materials with Elastic modulus of 2.4 GPa	ISO 527 \| 1 mm/min
Elongation	23.0 °C	6 % Show Supplier Material materials with Elongation of 6 %	ISO 527 \| yield, 50 mm/min
Flexural modulus	23.0 °C	2.3 GPa Show Supplier Material materials with Flexural modulus of 2.3 GPa	ISO 178 \| 2 mm/min
Flexural strength	23.0 °C	90 MPa Show Supplier Material materials with Flexural strength of 90 MPa	ISO 178 \| yield, 2 mm/min
Hardness, Ball Indentation	23.0 °C	95 MPa Show Supplier Material materials with Hardness, Ball Indentation of 95 MPa	ISO 2039-1 \| H358/30
Hardness, Rockwell M	23.0 °C	70 [-] Show Supplier Material materials with Hardness, Rockwell M of 70 [-]	ASTM D 785 \|
Hardness, Rockwell R	23.0 °C	118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-]	ASTM D 785
Impact strength, Charpy notched	23.0 °C	14 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 14 kJ/m²	ISO 179/1eA \| V-notch Edgew 80103 sp=62mm, -30°C
Impact strength, Izod notched	23.0 °C	12 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 12 kJ/m²	ISO 180/1A \| notched 80103, -30°C
Impact strength, Izod notched, ASTM	23.0 °C	801 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 801 J/m	ASTM D 256 \| notched, 23°C
Impact strength, Izod unnotched, ASTM	23.0 °C	3204 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m	ASTM D 4812 \| 23°C
Instrumented Impact, Total Energy	23.0 °C	70 J Show Supplier Material materials with Instrumented Impact, Total Energy of 70 J	ASTM D 3763 \| 23°C
Taber Abrasion	23.0 °C	10 mg/1000cy Show Supplier Material materials with Taber Abrasion of 10 mg/1000cy	ASTM D 1044 \| CS-17, 1 kg
Tensile strength	23.0 °C	63 MPa Show Supplier Material materials with Tensile strength of 63 MPa	ISO 527 \| yield, 50 mm/min
Impact strength, Charpy unnotched	ISO 179/1eU \| Unnotch Edgew 80103 sp=62mm, 23°C
Impact strength, Izod unnotched	ISO 180/1U \| 80103, 23°C

Thermal

Property	Temperature	Value	Comment
Ball Pressure Test		nan	IEC 60695-10-2 \| 125°C +/- 2°C
Coefficient of thermal expansion	23.0 °C	7E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 7E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature		125 - 136 °C Show Supplier Material materials with Heat deflection temperature of 125 - 136 °C
Heat deflection temperature, 0.45 MPa		136 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 136 °C	ISO 75/Be \| Edgew 120104 sp=100mm
Heat deflection temperature, 1.80 MPa		125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C	ISO 75/Ae \| Edgew 120104 sp=100mm
Relative temperature index, electrical		130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C	UL 746B
Relative temperature index, mechanical impact		130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C	UL 746B
Relative temperature index, mechanical strength		130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C	UL 746B
Specific heat capacity	23.0 °C	1.25E-3 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 1.25E-3 J/(kg·K)	ASTM C 351
Thermal conductivity	23.0 °C	0.2 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.2 W/(m·K)	ISO 8302
Vicat softening temperature		142 °C Show Supplier Material materials with Vicat softening temperature of 142 °C	ISO 306 \| Rate B/120
Flammability	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228425- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.7mm UL 94 <br> UV-light, water exposure/immersion: F2- UL 746C <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=541348- - <br> UL Yellow Card Link 3: https://iq.ul.com/ul/cert.aspx?ULID=220939- -

Electrical

Property	Temperature	Value	Comment
Comparative tracking index	23.0 °C	3 V Show Supplier Material materials with Comparative tracking index of 3 V	UL 746A \| (UL) {PLC}
Dielectric constant, 1MHz	23.0 °C	2.96 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 2.96 [-]	ASTM D 150
Dielectric constant, 60Hz	23.0 °C	3.17 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.17 [-]	ASTM D 150 \| 50/60 Hz
Dielectric strength	23.0 °C	14.9 kV/mm Show Supplier Material materials with Dielectric strength of 14.9 kV/mm	ASTM D 149 \| in air, 3.2 mm
Dissipation factor, 1MHz	23.0 °C	0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-]	ASTM D 150 \|
Dissipation factor, 50Hz	23.0 °C	9E-4 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 9E-4 [-]	ASTM D 150 \| 50/60 Hz
High Amp Arc Ignition	23.0 °C	1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm	≥, UL 746A \| PLC 0
High Volt Arc Track Rate	23.0 °C	2 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 2 PLC Code	UL 746A \| (PLC)
Hot-Wire Ignition	23.0 °C	1.1 mm Show Supplier Material materials with Hot-Wire Ignition of 1.1 mm	≥, UL 746A \| PLC 3
Volume resistivity	23.0 °C	1.00E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+17 Ω·cm	>, ASTM D 257

Optical

Property	Value	Comment
Haze	1 % Show Supplier Material materials with Haze of 1 %	ASTM D 1003 \| 2.54 mm
Refractive index	1.59 [-] Show Supplier Material materials with Refractive index of 1.59 [-]	ASTM D542
Transmission	88 % Show Supplier Material materials with Transmission of 88 %	ASTM D 1003 \| 2.54 mm

Rheological Properties

Property	Temperature	Value	Comment
Melt mass-flow rate		10.5 g/10min Show Supplier Material materials with Melt mass-flow rate of 10.5 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Melt volume-flow rate		11 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 11 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg
Shrinkage	23.0 °C	0.3 % Show Supplier Material materials with Shrinkage of 0.3 %	SABIC method \| 3.2 mm

Technological properties

Property
Application areas	Enclosure/Housing/Cover, Individual Equiptment, Forward Lighting, Building Accessory, Cluster, Data Transfer, Document Handling, LED Lighting, Rear/Signal Lighting, Wireless Communications, Irrigation
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 120°C Drying Time: 2 to 4.0hrs Drying Time (Cumulative): 48hrs Maximum Moisture Content: 0.02% Melt Temperature: 280 to 315.0°C Nozzle Temperature: 270 to 310.0°C Front - Zone 3 Temperature: 280 to 315.0°C Middle - Zone 2 Temperature: 270 to 305.0°C Rear - Zone 1 Temperature: 270 to 295.0°C Mold Temperature: 70 to 110.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.