Property | Temperature | Value | Comment |
---|---|---|---|
Density | 23.0 °C | 1.53 g/cm³ Show Supplier Material materials with Density of 1.53 g/cm³ | ASTM D 792 |
Limiting oxygen index | 23.0 °C | 19 % Show Supplier Material materials with Limiting oxygen index of 19 % | |
Moisture absorption | 23.0 °C | 0.08 % Show Supplier Material materials with Moisture absorption of 0.08 % | ISO 62 | (23°C / 50% RH) |
Relative density | 23.0 °C | 1.53 [-] Show Supplier Material materials with Relative density of 1.53 [-] | ASTM D 792 | |
Specific volume | 23.0 °C | 0.65 cm³/g Show Supplier Material materials with Specific volume of 0.65 cm³/g | ASTM D 792 |
Water absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Water absorption of 0.06 % | ASTM D 570 | (23°C/24hrs) |
Mechanical
Property | Temperature | Value | Comment |
---|---|---|---|
Elastic modulus | 23.0 °C | 9.3 GPa Show Supplier Material materials with Elastic modulus of 9.3 GPa | ISO 527 | 1 mm/min |
Elongation | 23.0 °C | 2 % Show Supplier Material materials with Elongation of 2 % | ISO 527 | break, 5 mm/min |
Flexural modulus | 23.0 °C | 8.5 GPa Show Supplier Material materials with Flexural modulus of 8.5 GPa | ISO 178 | 2 mm/min |
Flexural strength | 23.0 °C | 195 MPa Show Supplier Material materials with Flexural strength of 195 MPa | ISO 178 | yield, 2 mm/min |
Hardness, Ball Indentation | 23.0 °C | 122 MPa Show Supplier Material materials with Hardness, Ball Indentation of 122 MPa | ISO 2039-1 | H358/30 |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ISO 2039-2 |
Impact strength, Charpy notched | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Impact strength, Charpy notched of 5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Charpy unnotched | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Charpy unnotched of 45 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Impact strength, Izod notched | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Impact strength, Izod notched of 7 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Impact strength, Izod unnotched of 45 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 801 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 801 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, Total Energy of 8 J | ASTM D 3763 | 23°C |
Taber Abrasion | 23.0 °C | 19 mg/1000cy Show Supplier Material materials with Taber Abrasion of 19 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Tensile strength | 23.0 °C | 125 MPa Show Supplier Material materials with Tensile strength of 125 MPa | ISO 527 | break, 5 mm/min |
Thermal
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Passs | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coefficient of thermal expansion | 23.0 °C | 2.52E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 2.52E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coefficient of thermal expansion, transverse | 23.0 °C | 1.2E-4 1/K Show Supplier Material materials with Coefficient of thermal expansion, transverse of 1.2E-4 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Flammability Index | 800 °C Show Supplier Material materials with Glow Wire Flammability Index of 800 °C | ||||
Glow Wire Ignition Temperature | 825 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature | 204 - 217 °C Show Supplier Material materials with Heat deflection temperature of 204 - 217 °C | ||||
Heat deflection temperature, 0.45 MPa | 217 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 204 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 140 °C Show Supplier Material materials with Relative temperature index, electrical of 140 °C | UL 746B | |||
Relative temperature index, mechanical impact | 140 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Thermal conductivity | 23.0 °C | 0.19 W/(m·K) Show Supplier Material materials with Thermal conductivity of 0.19 W/(m·K) | ISO 8302 | ||
Vicat softening temperature | 223 °C Show Supplier Material materials with Vicat softening temperature of 223 °C | ISO 306 | Rate A/50 | |||
Flammability | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103952715- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.84mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 775°C IEC 60695-2-13 <br> Glow Wire Ignitability Temperature, 1.5 mm: 775°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.0 mm: 750°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.5 mm: 750°C IEC 60695-2-12 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103938351- - |
Electrical
Property | Temperature | Value | Comment |
---|---|---|---|
Comparative tracking index | 23.0 °C | 0 V Show Supplier Material materials with Comparative tracking index of 0 V | UL 746A | (UL) {PLC} |
Dielectric constant, 100Hz | 23.0 °C | 3.8 [-] Show Supplier Material materials with Dielectric constant, 100Hz of 3.8 [-] | ASTM D 150 |
Dielectric constant, 1MHz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Dielectric constant, 1MHz of 3.1 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.1 [-] | IEC 60250 | 50/60 Hz |
Dielectric strength | 23.0 °C | 16 kV/mm Show Supplier Material materials with Dielectric strength of 16 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Dissipation factor, 100Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1E-3 [-] | IEC 60250 | 50/60 Hz |
High Amp Arc Ignition | 23.0 °C | 0.38 mm Show Supplier Material materials with High Amp Arc Ignition of 0.38 mm | ≥, UL 746A | PLC 2 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 1 |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Melt mass-flow rate | 17 g/10min Show Supplier Material materials with Melt mass-flow rate of 17 g/10min | ISO 1133 | 250°C/2.16 kg | |
Melt volume-flow rate | 13 cm³/10min Show Supplier Material materials with Melt volume-flow rate of 13 cm³/10min | ISO 1133 | MVR at 250°C/2.16 kg | |
Shrinkage | 23.0 °C | 0.3 % Show Supplier Material materials with Shrinkage of 0.3 % | SABIC method | on tensile bar |
Shrinkage, transverse | 23.0 °C | 0.5 % Show Supplier Material materials with Shrinkage, transverse of 0.5 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |