ASTM A182 Grade F6a

ASTM A182 Grade F6a-1

ASTM A182 Grade F6a-2

ASTM A182 Grade F6a-3

ASTM A182 Grade F6a-4

Search results

Materials


Mechanical

Reduction of area (%)
Hardness, Brinell ([-])
Yield strength (MPa)
Tensile strength (MPa)

You should select at least 1 property to see the chart!

ASTM A182 Grade F6a-1

ASTM A182 Grade F6a-2

ASTM A182 Grade F6a-3

ASTM A182 Grade F6a-4

ASTM A182 Grade F6a-1

ASTM A182 Grade F6a-2

ASTM A182 Grade F6a-3

ASTM A182 Grade F6a-4

Chemical composition

Element

Weight %

Comment

Fe

83.78 - 88.5 %

Cr

11.5 - 13.5 %

Mn

0 - 1 %

P

0 - 0.04 %

C

0 - 0.15 %

More

Element

Weight %

Comment

Fe

83.78 - 88.5 %

Cr

11.5 - 13.5 %

Mn

0 - 1 %

P

0 - 0.04 %

C

0 - 0.15 %

More

Element

Weight %

Comment

Fe

83.78 - 88.5 %

Cr

11.5 - 13.5 %

Mn

0 - 1 %

P

0 - 0.04 %

C

0 - 0.15 %

More

Element

Weight %

Comment

Fe

83.78 - 88.5 %

Cr

11.5 - 13.5 %

Mn

0 - 1 %

P

0 - 0.04 %

C

0 - 0.15 %

More

Mechanical

Reduction of area, Z

35 % at 20 °C

35 % at 20 °C

35 % at 20 °C

35 % at 20 °C

Hardness, Brinell, HB

0 - 187 [-] at 20 °C

0 - 229 [-] at 20 °C

0 - 302 [-] at 20 °C

0 - 321 [-] at 20 °C

Yield strength, YS

275 MPa at 20 °C

380 MPa at 20 °C

585 MPa at 20 °C

760 MPa at 20 °C

Tensile strength, Rm

485 MPa at 20 °C

585 MPa at 20 °C

760 MPa at 20 °C

895 MPa at 20 °C