Eigenschaften
Allgemein
| Property | Value | Comment | |
|---|---|---|---|
Carbon equivalent (CEV) | 0.43 [-] Show Supplier Material materials with Carbon equivalent (CEV) of 0.43 [-] | Indicative value | Product | |
Weld cracking parameter | 0.22 [-] Show Supplier Material materials with Weld cracking parameter of 0.22 [-] | Product | |
Carbon equivalent note | CEV = C + Mn/6 + (Cr+Mo+V)/5 + (Cu+Ni)/15 and PCM = C + Si/30 + (Cr+Mn+Cu)/20 + Ni/60 + Mo/15 + V/10 + 5B | ||
Mechanisch
| Property | Temperature | Value | Comment |
|---|---|---|---|
Dehnung | 22 % Show Supplier Material materials with Dehnung of 22 % | min. A5.65√So | for thickness 5-80 mm | Transverse | |
Kerbschlagenergie | -40 °C | 50 J Show Supplier Material materials with Kerbschlagenergie of 50 J | min. | for thickness 5-80 mm | Transverse |
Streckgrenze | 325 MPa Show Supplier Material materials with Streckgrenze of 325 MPa | min. | for thickness 63-80 mm | Transverse | |
335 MPa Show Supplier Material materials with Streckgrenze of 335 MPa | min. | for thickness 40-63 mm | Transverse | ||
345 MPa Show Supplier Material materials with Streckgrenze of 345 MPa | min. | for thickness 25-40 mm | Transverse | ||
355 MPa Show Supplier Material materials with Streckgrenze of 355 MPa | min. | for thickness 5-25 mm | Transverse | ||
Yield to strength ratio | 0.85 [-] Show Supplier Material materials with Yield to strength ratio of 0.85 [-] | max | for thickness 16-25 mm | Transverse | |
0.87 [-] Show Supplier Material materials with Yield to strength ratio of 0.87 [-] | max | for thickness 5-16 mm | Transverse | ||
Zugfestigkeit | 470 - 630 MPa Show Supplier Material materials with Zugfestigkeit of 470 - 630 MPa | for thickness 5-80 mm | Transverse |
Chemical properties
| Property | Value | Comment |
|---|---|---|
Aluminium | 0.015 - 0.055 % Show Supplier Material materials with Aluminium of 0.015 - 0.055 % | for thickness 5-100 mm |
Chrom | 0.2 % Show Supplier Material materials with Chrom of 0.2 % | max. | for thickness 5-100 mm |
Kohlenstoff | 0.12 % Show Supplier Material materials with Kohlenstoff of 0.12 % | max. | for thickness 5-100 mm |
Kupfer | 0.3 % Show Supplier Material materials with Kupfer of 0.3 % | max. | for thickness 5-100 mm |
Mangan | 1.65 % Show Supplier Material materials with Mangan of 1.65 % | max. | for thickness 5-100 mm |
Molybdän | 0.08 % Show Supplier Material materials with Molybdän of 0.08 % | max. | for thickness 5-100 mm |
Nickel | 0.7 % Show Supplier Material materials with Nickel of 0.7 % | max. | for thickness 5-100 mm |
Niobium | 0.03 % Show Supplier Material materials with Niobium of 0.03 % | max. | for thickness 5-100 mm |
Phosphor | 0.015 % Show Supplier Material materials with Phosphor of 0.015 % | max. | for thickness 5-100 mm |
Schwefel | 0.005 % Show Supplier Material materials with Schwefel of 0.005 % | max. | for thickness 5-100 mm |
Silizium | 0.15 - 0.55 % Show Supplier Material materials with Silizium of 0.15 - 0.55 % | for thickness 5-100 mm |
Stickstoff | 0.01 % Show Supplier Material materials with Stickstoff of 0.01 % | max. | for thickness 5-100 mm |
Titan | 0.025 % Show Supplier Material materials with Titan of 0.025 % | max. | for thickness 5-100 mm |
Vanadium | 0.06 % Show Supplier Material materials with Vanadium of 0.06 % | max. | for thickness 5-100 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Offshore structures such as platforms and equipment for new offshore windmill towers. | |
| Chemical composition | The above chemical properties are based on cast analysis data. Product analysis may be requested at the time of order. | |
| Delivery condtion | For the dimensions available please visit Dimension tables (see Table A). Table A with a thickness range as indicated in the Mechanical properties. | |
| Other | Available options Options available (after previous agreement): | |