Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.05 g/cm³ Show Supplier Material materials with Dichte of 1.05 g/cm³ | dry | ISO 1183 |
Moisture absorption | 1.8 % Show Supplier Material materials with Moisture absorption of 1.8 % | Sim. to ISO 62 | |
Wasserabsorption | 6 % Show Supplier Material materials with Wasserabsorption of 6 % | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Dehnung | 50 % Show Supplier Material materials with Dehnung of 50 % | cond., dry | ISO 527-1/-2 | min. | nominal | |
550 % Show Supplier Material materials with Dehnung of 550 % | dry | ISO 527-3 | Transverse | ||
610 % Show Supplier Material materials with Dehnung of 610 % | dry | ISO 527-3 | |||
Elastizitätsmodul | 1.8 GPa Show Supplier Material materials with Elastizitätsmodul of 1.8 GPa | cond. | ISO 527-1/-2 | ||
2 GPa Show Supplier Material materials with Elastizitätsmodul of 2 GPa | dry | ISO 527-1/-2 | |||
Elongation at yield | 4 % Show Supplier Material materials with Elongation at yield of 4 % | dry | ISO 527-2/-2 | ||
6 % Show Supplier Material materials with Elongation at yield of 6 % | cond. | ISO 527-1/-2 | |||
16 % Show Supplier Material materials with Elongation at yield of 16 % | dry | ISO 527-3 | |||
Elongation at yield, transverse | 16 % Show Supplier Material materials with Elongation at yield, transverse of 16 % | dry | ISO 527-3 | ||
Härte, Shore D | 67 [-] Show Supplier Material materials with Härte, Shore D of 67 [-] | dry | ISO 7619-1 | 15 seconds | |
Schlagfestigkeit, Charpy gekerbt | 23 °C | 20 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 20 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 23 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 23 kJ/m² | dry | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | No Break at 23°C | cond. | ISO 179/1eU | ||
Streckgrenze | 35 MPa Show Supplier Material materials with Streckgrenze of 35 MPa | dry | ISO 527-3 | Transverse | |
36 MPa Show Supplier Material materials with Streckgrenze of 36 MPa | cond. | ISO 527-1/-2 | |||
Tear force | 45 N Show Supplier Material materials with Tear force of 45 N | ISO 6383-2 | |||
55 N Show Supplier Material materials with Tear force of 55 N | ISO 6383-2 | Transverse | |||
Zugfestigkeit | 55 MPa Show Supplier Material materials with Zugfestigkeit of 55 MPa | dry | ISO 527-3 | Transverse | |
61 MPa Show Supplier Material materials with Zugfestigkeit of 61 MPa | dry | ISO 527-3 |
Thermisch
| Property | Value | Condition | Testing Standard | Pressure | Comment | ||||
|---|---|---|---|---|---|---|---|---|---|
Schmelzpunkt | 220 °C Show Supplier Material materials with Schmelzpunkt of 220 °C | dry | ISO 11357-1/-3 | 10°C/min | |||||
Vicat-Erweichungstemperatur | 128 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 128 °C | ISO 306 | 50°C/h 50N | ||||||
Wärmeformbeständigkeitstemperatur | 50 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 50 °C | dry | ISO 75-1/-2 | 2 MPa | |||||
80 °C Show Supplier Material materials with Wärmeformbeständigkeitstemperatur of 80 °C | dry | ISO 75-1/-2 | 0.45 MPa | ||||||
Entflammbarkeit | At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB | ||||||||
Elektrisch
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | cond. | IEC 60112 |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schmelzvolumenflussrate | 4 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 4 cm³/10min | dry | ISO 1133 | 235°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Fuel Management - Fuel Lines,Conveyor Belts and Pulleys,Underground Fuel Containment | |
| Certifications | European Food Contact | |
| Processing methods | Injection Molding: Extrusion: | |