Pebax® Rnew® 30R51 SA 01

Alternative und Handelsbezeichungen
TPA

Want to keep this datasheet? Save it now in your required format

Description

Polyether block Pebax® Rnew® 30R51 SA 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources.

Pebax® Rnew® 30R51 SA 01 resin is an inherently antistatic polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part. This grade is particularly recommended for PMMA matrices. This hydrophilic grade when extruded into either a thin film or laminated on to a substrate offers excellent permeability to moisture vapor while remaining waterproof. The percentage of renewable carbon according to ASTM D6866 is 41%

. Refractive index according to an internal method is 1.49.

Diese Materialdaten wurden von Arkema Technical Polymers zur Verfügung gestellt

Alle Daten beziehen sich auf Raumtemperatur soweit nicht anderweitig spezifiziert. SI Einheiten werden verwendt soweit nicht anderweitig spezifiziert.
Äquivalente Standards sind ähnlich zu einem oder mehreren Standards die der Anbieter angegeben hat. Manche äquivalente Standards können strikter sein oder außerhalb der Bedingungen des ursprünglichen Standards.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Eigenschaften

Allgemein

Property	Value	Condition	Testing Standard
Bio-based content	41 % Show Supplier Material materials with Bio-based content of 41 %
Dichte	1.01 g/cm³ Show Supplier Material materials with Dichte of 1.01 g/cm³	dry	ISO 1183
Moisture absorption	2.5 % Show Supplier Material materials with Moisture absorption of 2.5 %		Sim. to ISO 62
Wasserabsorption	20 % Show Supplier Material materials with Wasserabsorption of 20 %		Sim. to ISO 62

Mechanisch

Property	Value	Condition	Testing Standard	Comment
Dehnung	50 % Show Supplier Material materials with Dehnung of 50 %	cond.	ISO 527-1/-2	min.
Elastizitätsmodul	0.059 GPa Show Supplier Material materials with Elastizitätsmodul of 0.059 GPa	cond.	ISO 527-1/-2
Härte, Shore D	30 [-] Show Supplier Material materials with Härte, Shore D of 30 [-]	dry	ISO 7619-1	15 seconds

Thermisch

Property	Value	Condition	Testing Standard	Comment
Schmelzpunkt	150 °C Show Supplier Material materials with Schmelzpunkt of 150 °C	dry	ISO 11357-1/-3	10°C/min

Elektrisch

Property	Value	Condition	Testing Standard
Surface resistivity	1e+08 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+08 Ω/sq	cond.	IEC 60093
Volume resistivity	1e+08 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+08 Ω·cm	cond.	IEC 60093
	1e+10 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+10 Ω·cm	dry	IEC 60093

Technological properties

Property

Application areas

Breathable Films - Housewrap,Permanent Antistatic Solutions,Eyewear Frames,Permanent Antistatic Solutions E&E

Processing methods

Injection Molding:

Typical melt temperature (Min / Recommended / Max): 200°C / 240°C / 270°C.

Typical mold temperature: 25–60°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.

Extrusion:

Typical melt temperature (Min / Recommended / Max): 210°C / 220°C / 230°C.

Drying time and temperature (only necessary for bags opened for more than two hours): 4-6 hours at 65-75°C.