Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Dichte | 1.02 g/cm³ Show Supplier Material materials with Dichte of 1.02 g/cm³ | dry | ISO 1183 |
Wasserabsorption | 1.4 % Show Supplier Material materials with Wasserabsorption of 1.4 % | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Dehnung | 50 % Show Supplier Material materials with Dehnung of 50 % | cond., dry | ISO 527-1/-2 | min. | nominal | |
Elastizitätsmodul | 0.55 GPa Show Supplier Material materials with Elastizitätsmodul of 0.55 GPa | cond. | ISO 527-1/-2 | ||
0.62 GPa Show Supplier Material materials with Elastizitätsmodul of 0.62 GPa | dry | ISO 527-1/-2 | |||
Elongation at yield | 20 % Show Supplier Material materials with Elongation at yield of 20 % | cond., dry | ISO 527-1/-2 | ||
Schlagfestigkeit, Charpy gekerbt | -30 °C | 3 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 3 kJ/m² | cond., dry | ISO 179/1eA | |
23 °C | 9 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 9 kJ/m² | dry | ISO 179/1eA | ||
23 °C | 14 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 14 kJ/m² | cond. | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | No Break at 23 and -30°C | dry and cond. | ISO 179/1eU | ||
Streckgrenze | 24 MPa Show Supplier Material materials with Streckgrenze of 24 MPa | cond. | ISO 527-1/-2 | ||
42 MPa Show Supplier Material materials with Streckgrenze of 42 MPa | dry | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 0.00012 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 0.00012 1/K | dry | ISO 11359-1/-2 | |
Schmelzpunkt | 173 °C Show Supplier Material materials with Schmelzpunkt of 173 °C | dry | ISO 11357-1/-3 | 10°C/min |
Vicat-Erweichungstemperatur | 134 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 134 °C | ISO 306 | 50°C/h 50N |
Elektrisch
| Property | Value | Condition | Frequency | Testing Standard |
|---|---|---|---|---|
Dielektrizitätskonstante | 4 [-] Show Supplier Material materials with Dielektrizitätskonstante of 4 [-] | dry | 1MHz | IEC 60250 |
8 [-] Show Supplier Material materials with Dielektrizitätskonstante of 8 [-] | dry | 100Hz | IEC 60250 | |
Durchschlagfestigkeit | 26 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 26 kV/mm | cond. | IEC 60243-1 | |
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | cond. | IEC 60112 | |
Surface resistivity | 1e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+12 Ω/sq | cond. | IEC 60093 | |
Verlustfaktor | 0.0595 [-] Show Supplier Material materials with Verlustfaktor of 0.0595 [-] | dry | 1MHz | IEC 60250 |
0.201 [-] Show Supplier Material materials with Verlustfaktor of 0.201 [-] | dry | 100Hz | IEC 60250 | |
Volume resistivity | 1e+10 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+10 Ω·cm | cond. | IEC 60093 |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schmelzvolumenflussrate | 44 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 44 cm³/10min | dry | ISO 1133 | 235°C/2.16kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Connectors,Sports Equipment | |
| Processing methods | Injection Molding: | |