Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Bio-based content | 97 % Show Supplier Material materials with Bio-based content of 97 % | ||
Dichte | 1.23 g/cm³ Show Supplier Material materials with Dichte of 1.23 g/cm³ | dry | ISO 1183 |
Wasserabsorption | 1.3 % Show Supplier Material materials with Wasserabsorption of 1.3 % | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Dehnung | 40 % Show Supplier Material materials with Dehnung of 40 % | cond. | ISO 527-1/-2 | ||
Elastizitätsmodul | 1.9 GPa Show Supplier Material materials with Elastizitätsmodul of 1.9 GPa | cond. | ISO 527-1/-2 | ||
Härte, Shore D | 71 [-] Show Supplier Material materials with Härte, Shore D of 71 [-] | dry | ISO 7619-1 | 15 seconds | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 5 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 5 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 6 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 6 kJ/m² | cond. | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 96 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 96 kJ/m² | cond. | ISO 179/1eU | |
23 °C | 96 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 96 kJ/m² | cond. | ISO 179/1eU | ||
Zugfestigkeit | 31 MPa Show Supplier Material materials with Zugfestigkeit of 31 MPa | cond. | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 7e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 7e-05 1/K | dry | ISO 11359-1/-2 | ||||
Schmelzpunkt | 189 °C Show Supplier Material materials with Schmelzpunkt of 189 °C | dry | ISO 11357-1/-3 | 10°C/min | |||
Vicat-Erweichungstemperatur | 165 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 165 °C | ISO 306 | 50°C/h 50N | ||||
Entflammbarkeit | At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB | ||||||
Elektrisch
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Durchschlagfestigkeit | 40 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 40 kV/mm | cond. | IEC 60243-1 |
Kriechstromfestigkeit | 600 V Show Supplier Material materials with Kriechstromfestigkeit of 600 V | cond. | IEC 60112 |
Surface resistivity | 1e+14 Ω/sq Show Supplier Material materials with Surface resistivity of 1e+14 Ω/sq | cond. | IEC 60093 |
Volume resistivity | 1e+12 Ω·cm Show Supplier Material materials with Volume resistivity of 1e+12 Ω·cm | cond. | IEC 60093 |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schmelzvolumenflussrate | 20 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 20 cm³/10min | dry | ISO 1133 | 235°C/5kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Main applications: Packaging: This grade is delivered dried in sealed packaging (25 kg bags) ready to be processed. Shelf life: Two years from the delivery. For any use above this limit, please refer to our technical services. | |
| Fillers | 30% Glass Bead | |
| Processing methods | Injection Molding: | |