Eigenschaften
Allgemein
| Property | Value | Condition | Testing Standard |
|---|---|---|---|
Bio-based content | 86 % Show Supplier Material materials with Bio-based content of 86 % | ||
Dichte | 1.22 g/cm³ Show Supplier Material materials with Dichte of 1.22 g/cm³ | dry | ISO 1183 |
Sauerstoffindex | 22 % Show Supplier Material materials with Sauerstoffindex of 22 % | dry | ISO 4589-1/-2 |
Wasserabsorption | 1.2 % Show Supplier Material materials with Wasserabsorption of 1.2 % | Sim. to ISO 62 |
Mechanisch
| Property | Temperature | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|---|
Dehnung | 5 % Show Supplier Material materials with Dehnung of 5 % | cond. | ISO 527-1/-2 | ||
Elastizitätsmodul | 6.1 GPa Show Supplier Material materials with Elastizitätsmodul of 6.1 GPa | cond. | ISO 527-1/-2 | ||
Härte, Shore D | 74 [-] Show Supplier Material materials with Härte, Shore D of 74 [-] | dry | ISO 7619-1 | 15 seconds | |
Schlagfestigkeit, Charpy gekerbt | -30 °C | 10 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 10 kJ/m² | cond. | ISO 179/1eA | |
23 °C | 13 kJ/m² Show Supplier Material materials with Schlagfestigkeit, Charpy gekerbt of 13 kJ/m² | cond. | ISO 179/1eA | ||
Schlagzähigkeit, Charpy ungekerbt | -30 °C | 83 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 83 kJ/m² | cond. | ISO 179/1eU | |
23 °C | 74 kJ/m² Show Supplier Material materials with Schlagzähigkeit, Charpy ungekerbt of 74 kJ/m² | cond. | ISO 179/1eU | ||
Zugfestigkeit | 108 MPa Show Supplier Material materials with Zugfestigkeit of 108 MPa | cond. | ISO 527-1/-2 |
Thermisch
| Property | Value | Condition | Testing Standard | Comment | |||
|---|---|---|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 5e-05 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 5e-05 1/K | dry | ISO 11359-1/-2 | ||||
Schmelzpunkt | 186 °C Show Supplier Material materials with Schmelzpunkt of 186 °C | dry | ISO 11357-1/-3 | 10°C/min | |||
Vicat-Erweichungstemperatur | 170 °C Show Supplier Material materials with Vicat-Erweichungstemperatur of 170 °C | ISO 306 | 50°C/h 50N | ||||
Entflammbarkeit | At thickness 1.6 mm IEC 60695-11-10: HB, At thickness 3.2 mm IEC 60695-11-10: HB | ||||||
Elektrisch
| Property | Value | Condition | Frequency | Testing Standard |
|---|---|---|---|---|
Dielektrizitätskonstante | 5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 5 [-] | dry | 100Hz | IEC 60250 |
5 [-] Show Supplier Material materials with Dielektrizitätskonstante of 5 [-] | dry | 1MHz | IEC 60250 | |
Durchschlagfestigkeit | 22 kV/mm Show Supplier Material materials with Durchschlagfestigkeit of 22 kV/mm | cond. | IEC 60243-1 | |
Kriechstromfestigkeit | 300 V Show Supplier Material materials with Kriechstromfestigkeit of 300 V | cond. | IEC 60112 | |
Surface resistivity | 6e+12 Ω/sq Show Supplier Material materials with Surface resistivity of 6e+12 Ω/sq | cond. | IEC 60093 | |
Verlustfaktor | 0.0208 [-] Show Supplier Material materials with Verlustfaktor of 0.0208 [-] | dry | 1MHz | IEC 60250 |
0.0334 [-] Show Supplier Material materials with Verlustfaktor of 0.0334 [-] | dry | 100Hz | IEC 60250 | |
Volume resistivity | 2e+11 Ω·cm Show Supplier Material materials with Volume resistivity of 2e+11 Ω·cm | cond. | IEC 60093 |
Rheological Properties
| Property | Value | Condition | Testing Standard | Comment |
|---|---|---|---|---|
Schmelzvolumenflussrate | 9 cm³/10min Show Supplier Material materials with Schmelzvolumenflussrate of 9 cm³/10min | dry | ISO 1133 | 235°C/5kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Chemical Process Industry - Injection Molding | |
| Fillers | 30% Glass Fiber and Carbon Black | |
| Processing methods | Injection Molding: | |