Eigenschaften
Allgemein
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Relative Dichte | 3 [-] Show Supplier Material materials with Relative Dichte of 3 [-] | Archimedes | min. |
Mechanisch
| Property | Value | Testing Standard | Comment |
|---|---|---|---|
Biegefestigkeit | 230 MPa Show Supplier Material materials with Biegefestigkeit of 230 MPa | EN DIN 843-1 | min. | 4-point bending 20/40 mm | spacing 46x4x3 mm specimen size | ground surface 20°C |
Elastizitätsmodul | 310 GPa Show Supplier Material materials with Elastizitätsmodul of 310 GPa | EN DIN 843-2 | min. | Ultrasonic |
Hardness, Vickers, 1 | 2243 [-] Show Supplier Material materials with Hardness, Vickers, 1 of 2243 [-] | Fracture surface ground and polished | |
Plane-Strain Fracture Toughnes | 2.4 MPa·√m Show Supplier Material materials with Plane-Strain Fracture Toughnes of 2.4 MPa·√m | EN DIN 14425 | SEVNB 4-point bending 20/40 mm | Spacing 46x4x3 mm | Specimen size 20°C |
Poissonzahl | 0.15 [-] Show Supplier Material materials with Poissonzahl of 0.15 [-] | EN DIN 843-2 | |
Weibull-Modul | 15 [-] Show Supplier Material materials with Weibull-Modul of 15 [-] | 4P | min. |
Thermisch
| Property | Temperature | Value | Testing Standard | Comment |
|---|---|---|---|---|
Koeffizient der thermischen Ausdehnung | 3.7e-06 - 4.1e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3.7e-06 - 4.1e-06 1/K | 20-200°C | ||
3.9e-06 - 4.3e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 3.9e-06 - 4.3e-06 1/K | 20-400°C | |||
4.2e-06 - 4.6e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.2e-06 - 4.6e-06 1/K | 20-600°C | |||
4.5e-06 - 4.9e-06 1/K Show Supplier Material materials with Koeffizient der thermischen Ausdehnung of 4.5e-06 - 4.9e-06 1/K | 20-1000°C | |||
Spezifische Wärmekapazität | 20 °C | 0.66 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 0.66 J/(kg·K) | ISO 11357-1 | |
100 °C | 0.87 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 0.87 J/(kg·K) | ISO 11357-1 | ||
Wärmeleitfähigkeit | 140 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 140 W/(m·K) | DIN EN 821 | min. | Xe-flash sample | 16*16mm² material specific thickness |
Technological properties
| Property | ||
|---|---|---|
| Other | Sintered silicon carbide is created when prepressed and very soft SiC granulate is sintered at a temperature of more than 2,000 °C, when very strong sintering bonds between the material grains are formed. Firstly, there is lattice densification, then the porosity is lowered, and finally, sintering bonds between the grains of SiC are formed. This firing process has considerable product shrinkage of about 20 %. The final material is single-phase with higher hardness, heat and chemical resistance than SiSiC. | |