Allgemein
Property | Value | Comment |
---|---|---|
Dichte | 3.73 g/cm³ Show Supplier Material materials with Dichte of 3.73 g/cm³ | |
Oberflächenrauigkeit | 0.8 μm Show Supplier Material materials with Oberflächenrauigkeit of 0.8 μm | as fired surface |
Wasserabsorption | 0.1 % Show Supplier Material materials with Wasserabsorption of 0.1 % |
Mechanisch
Property | Value | Testing Standard | Comment |
---|---|---|---|
Biegefestigkeit | 300 MPa Show Supplier Material materials with Biegefestigkeit of 300 MPa | DR sigma 0 | 0.63-1.00 mm thickness | rings 6 / 12 mm |
Thermisch
Property | Temperature | Value | Comment |
---|---|---|---|
Spezifische Wärmekapazität | 20 °C | 0.7 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 0.7 J/(kg·K) | |
100 °C | 0.9 J/(kg·K) Show Supplier Material materials with Spezifische Wärmekapazität of 0.9 J/(kg·K) | ||
Wärmeleitfähigkeit | 20 °C | 22 W/(m·K) Show Supplier Material materials with Wärmeleitfähigkeit of 22 W/(m·K) | Xe-flash | sample 16*16mm² | material specific thickness ≤ 3.5mm |
Elektrisch
Property | Temperature | Value | Frequency | Comment |
---|---|---|---|---|
Dielektrizitätskonstante | 8.3 - 11.3 [-] Show Supplier Material materials with Dielektrizitätskonstante of 8.3 - 11.3 [-] | 1 GHz, 10 MHz, 100 MHz | 2mm thickness | Ra ≤ 0.4μm | |
Verlustfaktor | 0.01 [-] Show Supplier Material materials with Verlustfaktor of 0.01 [-] | 1 GHz, 10 MHz, 100 MHz | max. | 2mm thickness | Ra ≤ 0.4μm | |
spezifischer Widerstand | 20 °C | 1e+11 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1e+11 Ω·m | ||
200 °C | 1e+09 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1e+09 Ω·m | |||
400 °C | 1e+07 Ω·m Show Supplier Material materials with spezifischer Widerstand of 1e+07 Ω·m | |||
600 °C | 100000 Ω·m Show Supplier Material materials with spezifischer Widerstand of 100000 Ω·m |
Technological properties
Property | ||
---|---|---|
Application areas | CeramTec uses Rubalit® alumina ceramics for CeramCore cores for metal-oxide, carbon-film, metal-layered, thin-film and wire-wound resistors. The fine structures of Rubalit® 600, 702 und 708 play a vital role in delivering very high and consistent surface quality. Using Rubalit® 600, 702 und 708 as core materials help create resistors with a lower noise factor and more stable resistance, increases resistance against electrical shock loads and improves reliability in laser trimming. This makes it possible to achieve higher integration density while simultaneously ensuring higher power density. CeramTec boasts decades of manufacturing experience, enabling the company to produce ceramic parts for passive components with tight dimensional tolerances while delivering very high surface quality even for large-scale production with quantities ranging in the billions. | |
Chemical composition | The material main component is Al₂O₃ with 95.8% content. Residue mainly consists of MgO, SiO2 and CaO and traces of other elements. |